Disertación de Maestría
DOI
10.11606/D.3.2009.tde-11082010-145038
Documento
Autor
Nombre completo
Elizabeth Rodrigues Rangel Roriz
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Tenório, Jorge Alberto Soares (Presidente)
De Lazzari, Claudio Parra
Espinosa, Denise Crocce Romano
Título en portugués
Reciclagem de pilhas: recuperação do manganês na forma do dióxido de manganês eletrolítico.
Palabras clave en portugués
Eletrodeposição
Manganês
Reciclagem de resíduos urbanos
Resumen en portugués
Neste trabalho, buscou-se verificar a possibilidade de, com a utilização do processo eletrolítico, se obter dióxido de manganês a partir da reciclagem de pilhas e baterias exauridas, visto a grande demanda por produtos que utilizam esse mineral. Utilizou-se, para tanto, uma solução eletrolítica que continha os íons metálicos: Ca (270mg/L), Ni (3000 mg/L), Co (630 mg/L), Mn(115300 mg/L), Ti (400 mg/L) e Pb (20 mg/L) em meio de ácido sulfúrico, sintetizada, seguindo-se dados de pesquisa anterior. A produção do dióxido de manganês eletrolítico (DME) foi realizada galvanostaticamente, com a utilização de uma fonte estabilizada que monitorava o potencial do eletrodo de trabalho. Utilizaram-se, preliminarmente, um eletrodo de trabalho de chumbo e dois contra-eletrodos de grafite, à temperatura de 98 ºC (±2ºC) e densidade de corrente de 1,69 A.dm-2. Após a verificação preliminar da possibilidade de obtenção do DME, repetiu-se sistematicamente o processo, aplicando-se variações de densidade de corrente (0,61 A.dm-2 a 1,93 A.dm-2) e de pH (0,00 a 1,20). O material obtido com essas variações foi analisado através dos processos de espectrometria de fluorescência de raios-X, difração de raios-X, área superficial específica pelo método BET e microscopia eletrônica de varredura (MEV). Os melhores resultados quanto a eficiência de corrente, pureza e área superficial se obtiveram com densidade de corrente entre 1,02 A.dm-2 e 1,39 A.dm-2 e com pH 0,50. Em todos os experimentos, como comprova a análise de difração de raios-X, foi constatada a obtenção da variedade alotrópica -MnO2, uma das formas viáveis para utilização na fabricação de pilhas. Os resultados apontam para a viabilidade desse processo de reciclagem como alternativa diante da escassez de fontes naturais de MnO2 com características compatíveis com a aplicação em questão e como forma de diminuição da poluição ambiental causada pelo descarte de pilhas e baterias.
Título en inglés
Recycling of batteries: recovery of manganese in the form of electrolytic manganese dioxide.
Palabras clave en inglés
Electroplating
Manganese
Recycling waste
Resumen en inglés
Considering the growing demand for products containing manganese in its composition, this work seeks to verify the possibility of using depleted batteries as a source of manganese applying the electrolytic process. It was used an electrolyte solution containing the metal ions: Ca (270mg / L), Ni (3000 mg / L), Co (630 mg / L), Mn (115300 mg / L), Ti (400 mg / L) and Pb (20 mg / L) in concentrated sulfuric acid, following data from previous research. The production of electrolytic manganese dioxide (EMD) was performed through galvanization using a stabilized source that monitored the potential of the working electrode. It was preliminary used an electrode of lead and two counter electrodes of graphite at a temperature of 98ºC (± 2ºC) and current density of 1.69A.dm-2. After preliminary verifying the possibility of obtaining electrolytic manganese dioxide (EMD), the process was systematically repeated, applying different current density (0.61A.dm-2 to 2.51A.dm-2) and pH (0.00 to 1.20). The material obtained at these variations was analyzed through the process of X-ray fluorescence spectrometry, X-ray diffraction, specific surface area (BET) and scanning electron microscopy (SEM). The best values referring to current efficiency, level of purity and specific surface area were obtained with the current density ranging between 1.02 A.dm-2 and 1.39 A.dm-2, and pH 0.50. In any of the tested electrolysis conditions the -MnO2 structure was obtained as evidenced by the diffraction of X-rays analysis. The results indicate the feasibility of this recycling process as an alternative before shortage of natural sources of MnO2 and as a means of reducing environmental pollution caused by the disposal of batteries.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-09-16
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • RORIZ, E. R. R., et al. Reciclagem de pilhas: recuperação do manganês na forma de dióxido de manganês eletrolítico. In 65º Congresso da ABM, Rio de Janeiro, 2010. 65º Congresso da ABM.São Paulo : ABM, 2010.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.