Thèse de Doctorat
DOI
10.11606/T.3.2016.tde-13072016-153629
Document
Auteur
Nom complet
Lorena Batista Caliman
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2015
Directeur
Jury
Gouvea, Douglas (Président)
Fonseca, Fabio Coral
Muccillo, Eliana Navarro dos Santos
Pallone, Eliria Maria de Jesus Agnolon
Steil, Marlu César
Titre en portugais
Sinterização flash do condutor catiônico beta-alumina sintetizada pelo método dos precursores poliméricos.
Mots-clés en portugais
Beta-alumina
Condutor catiônico
Eletrodo
Reação de eletrodo
Sinterização
Resumé en portugais
A beta-alumina de sódio é uma cerâmica condutora de íons Na+ utilizada como eletrólito sólido em baterias de sódio para armazenamento de energias intermitentes como energia solar e eólica. Devido ao alto teor de sódio, esse material é instável a altas temperaturas, podendo sofrer variações de composição durante a etapa de sinterização convencional que utiliza altas temperaturas por longos períodos de tempo. A sinterização flash é uma técnica de sinterização ativada por corrente elétrica que proporciona a densificação de compactos cerâmicos em poucos segundos, a temperaturas notavelmente mais baixas que as convencionais. Uma vez obrigatória a passagem de corrente elétrica através da amostra, a sinterização flash de qualquer material condutor parece bastante razoável. Não obstante, até o presente momento a maioria dos trabalhos publicados sobre o assunto aborda apenas condutores de vacância de oxigênio ou semicondutores, materiais compatíveis com eletrodos de platina (Pt). Nesse trabalho a sinterização flash de um condutor catiônico foi estudada utilizando-se a beta-alumina como material modelo. A beta-alumina foi sintetizada pelo método dos precursores poliméricos, caracterizada e então submetida à sinterização flash. O material de eletrodo padrão (platina) provou ser um eletrodo bloqueador em contato com a beta-alumina. O sucesso da sinterização flash foi determinado pela troca do material de eletrodo por prata (Ag), o que possibilitou uma reação eletroquímica reversível nas interfaces eletrodo-cerâmica e possibilitou a obtenção de um material densificado com morfologia e composição química homogêneas. Devido à metaestabilidade da beta-alumina, a atmosfera dos experimentos precisou ser alterada para manter a integridade desse material rico em um metal alcalino (Na+). A sinterização flash de um condutor catiônico é apresentada pela primeira vez na literatura e ressalta a importância da reação de eletrodo, que é um fator limitante para o sucesso da sinterização flash e precisa ser estudada e adaptada para cada tipo de material.
Titre en anglais
Flash sintering of the cationic conductor beta-alumina synthesized by the polymeric precursors method.
Mots-clés en anglais
Beta-alumina
Cationic conductor
Electrode reaction
Flash sintering
Resumé en anglais
Sodium beta-alumina is a Na+ ions conductor ceramic used as solid electrolyte in sodium batteries for energy storage in solar and eolic plants. Due to its high content of sodium, this material is instable at high temperatures and can suffer decomposition during conventional sintering (high temperatures for long periods of time). Flash sintering is an electric current activated sintering technique which promotes the densification of ceramic powder compacts in a few seconds at significantly lower temperatures than conventional sintering. Since in flash sintering the electric current flows through the sample, the flash sintering of any conductor material seems to be reasonable. Nevertheless, up to this date all published papers concern flash sintering of oxygen vacancies conductors or semi-conductors, materials which are compatible with platinum (Pt) electrodes. In this work the flash sintering of the cationic conductor betaalumina was studied. Beta-alumina was synthetized by the polymeric precursors method, characterized and then it was submitted to flash sintering. Platinum electrode was shown to be a blocking electrode for beta-alumina. Flash sintering success was determined by the change in electrode's material to silver (Ag), which made possible the reversible electrochemical reaction at the electrode-electrolyte interfaces and preserved chemical composition and morphology after flash. Due to this electrolyte metastability, atmosphere had to be changed in order to preserve the chemical composition of an alkali-rich (Na+) material such as beta-alumina. The flash sintering of a cationic conductor is shown for the first time in the literature and highlights the relevance of electrode reaction, which is a limiting point to the success of a flash sintering and needs to be well studied and adapted to each type of material.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-07-14
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.