Disertación de Maestría
DOI
Documento
Autor
Nombre completo
Mariane Yuka Tsubaki Oide
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2019
Director
Tribunal
Hui, Wang Shu (Presidente)
Fonseca, Fernando Josepetti
Mantovani, Gerson Luiz
Título en portugués
Sistemas poliméricos semicondutores para aplicação como camada ativa em LED.
Palabras clave en portugués
Filmes finos
Óptica eletrônica
Polímeros (Materiais)
Semicondutores
Resumen en portugués
Diodos poliméricos emissores de luz (PLEDs) foram produzidos utilizando poli(vinil-carbazol) (PVK), poli(2,7-(9,9-dioctilfluoreno)) (PFO) e poli((1,4-fenileno-2-flúor)-alt-2,7-(9,9-dioctilfluoreno)) (PFPF) dopados com diferentes concentrações de dopante fosforescente tris(2-fenilpiridinato) de irídio(III) [Ir(ppy)3] como camada ativa. Os resultados mostraram que o dispositivo a base de PFO dopado com 4% em massa de Ir(ppy)3 apresentou as maiores eficiências de corrente e de potência luminosa e o espectro eletromagnético do PLED a base de PVK puro apresentou emissão em 540 nm, sugerindo um desbalanceamento de cargas e emissão do óxido de zinco dopado com alumínio (AZO), camada injetora. Assim, estudos da influência da massa molar média do PVK e de sistemas híbridos PVK:AZO nas propriedades elétricas e ópticas dos PLEDs foram elaborados. Resultados mostraram que o AZO possui propriedades foto/eletroluminescentes e é responsável pela emissão larga na região do visível. Os dispositivos híbridos apresentaram emissão próxima ao branco puro, atingindo-se uma pureza de 0,19.
Título en inglés
Polymer semiconductors systems for application as active layer in led.
Palabras clave en inglés
AZO
Ir(ppy)3
Polyfluorene
PVK
WPLED.
Resumen en inglés
Polymer light emiting diodes (PLEDs) were manufactured using poly(9-vinylcarbazole) (PVK), poly(9,9-dioctylfluorene) (PFO) and poly(9,9-dioctylfluorene-alt-1,4-fluorphenylene) (PFPF) doped with different concentrations of tris-(2-phenylpyridinate) iridium(III) [Ir(ppy)3],a phosphorescent dye, as the active layer. Results showed that PFO based devices doped with 4 wt. % of Ir(ppy)3 presented the highest current and power efficiencies, and the PVK based devices' electroluminescence spectrum showed an emission centered at 540 nm, suggesting that a charge unbalance and light emission from the injection layer of aluminum doped zinc oxide (AZO) occurred. Therefore, studies based on the PVK:AZO system and different PVK's average molar masses were elaborated to observe the PLEDs' electrical and optical properties. Results showed that AZO is a photo/electroluminescent material and it is responsible for the broad emission in the visible range. The hybrid device showed near pure white light emission and its purity reached 0.19.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-04-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.