Mémoire de Maîtrise
DOI
Document
Auteur
Nom complet
Mariane Yuka Tsubaki Oide
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2019
Directeur
Jury
Hui, Wang Shu (Président)
Fonseca, Fernando Josepetti
Mantovani, Gerson Luiz
Titre en portugais
Sistemas poliméricos semicondutores para aplicação como camada ativa em LED.
Mots-clés en portugais
Filmes finos
Óptica eletrônica
Polímeros (Materiais)
Semicondutores
Resumé en portugais
Diodos poliméricos emissores de luz (PLEDs) foram produzidos utilizando poli(vinil-carbazol) (PVK), poli(2,7-(9,9-dioctilfluoreno)) (PFO) e poli((1,4-fenileno-2-flúor)-alt-2,7-(9,9-dioctilfluoreno)) (PFPF) dopados com diferentes concentrações de dopante fosforescente tris(2-fenilpiridinato) de irídio(III) [Ir(ppy)3] como camada ativa. Os resultados mostraram que o dispositivo a base de PFO dopado com 4% em massa de Ir(ppy)3 apresentou as maiores eficiências de corrente e de potência luminosa e o espectro eletromagnético do PLED a base de PVK puro apresentou emissão em 540 nm, sugerindo um desbalanceamento de cargas e emissão do óxido de zinco dopado com alumínio (AZO), camada injetora. Assim, estudos da influência da massa molar média do PVK e de sistemas híbridos PVK:AZO nas propriedades elétricas e ópticas dos PLEDs foram elaborados. Resultados mostraram que o AZO possui propriedades foto/eletroluminescentes e é responsável pela emissão larga na região do visível. Os dispositivos híbridos apresentaram emissão próxima ao branco puro, atingindo-se uma pureza de 0,19.
Titre en anglais
Polymer semiconductors systems for application as active layer in led.
Mots-clés en anglais
AZO
Ir(ppy)3
Polyfluorene
PVK
WPLED.
Resumé en anglais
Polymer light emiting diodes (PLEDs) were manufactured using poly(9-vinylcarbazole) (PVK), poly(9,9-dioctylfluorene) (PFO) and poly(9,9-dioctylfluorene-alt-1,4-fluorphenylene) (PFPF) doped with different concentrations of tris-(2-phenylpyridinate) iridium(III) [Ir(ppy)3],a phosphorescent dye, as the active layer. Results showed that PFO based devices doped with 4 wt. % of Ir(ppy)3 presented the highest current and power efficiencies, and the PVK based devices' electroluminescence spectrum showed an emission centered at 540 nm, suggesting that a charge unbalance and light emission from the injection layer of aluminum doped zinc oxide (AZO) occurred. Therefore, studies based on the PVK:AZO system and different PVK's average molar masses were elaborated to observe the PLEDs' electrical and optical properties. Results showed that AZO is a photo/electroluminescent material and it is responsible for the broad emission in the visible range. The hybrid device showed near pure white light emission and its purity reached 0.19.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2019-04-16
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.