• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Dissertação de Mestrado
DOI
Documento
Autor
Nome completo
Mariane Yuka Tsubaki Oide
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2019
Orientador
Banca examinadora
Hui, Wang Shu (Presidente)
Fonseca, Fernando Josepetti
Mantovani, Gerson Luiz
Título em português
Sistemas poliméricos semicondutores para aplicação como camada ativa em LED.
Palavras-chave em português
Filmes finos
Óptica eletrônica
Polímeros (Materiais)
Semicondutores
Resumo em português
Diodos poliméricos emissores de luz (PLEDs) foram produzidos utilizando poli(vinil-carbazol) (PVK), poli(2,7-(9,9-dioctilfluoreno)) (PFO) e poli((1,4-fenileno-2-flúor)-alt-2,7-(9,9-dioctilfluoreno)) (PFPF) dopados com diferentes concentrações de dopante fosforescente tris(2-fenilpiridinato) de irídio(III) [Ir(ppy)3] como camada ativa. Os resultados mostraram que o dispositivo a base de PFO dopado com 4% em massa de Ir(ppy)3 apresentou as maiores eficiências de corrente e de potência luminosa e o espectro eletromagnético do PLED a base de PVK puro apresentou emissão em 540 nm, sugerindo um desbalanceamento de cargas e emissão do óxido de zinco dopado com alumínio (AZO), camada injetora. Assim, estudos da influência da massa molar média do PVK e de sistemas híbridos PVK:AZO nas propriedades elétricas e ópticas dos PLEDs foram elaborados. Resultados mostraram que o AZO possui propriedades foto/eletroluminescentes e é responsável pela emissão larga na região do visível. Os dispositivos híbridos apresentaram emissão próxima ao branco puro, atingindo-se uma pureza de 0,19.
Título em inglês
Polymer semiconductors systems for application as active layer in led.
Palavras-chave em inglês
AZO
Ir(ppy)3
Polyfluorene
PVK
WPLED.
Resumo em inglês
Polymer light emiting diodes (PLEDs) were manufactured using poly(9-vinylcarbazole) (PVK), poly(9,9-dioctylfluorene) (PFO) and poly(9,9-dioctylfluorene-alt-1,4-fluorphenylene) (PFPF) doped with different concentrations of tris-(2-phenylpyridinate) iridium(III) [Ir(ppy)3],a phosphorescent dye, as the active layer. Results showed that PFO based devices doped with 4 wt. % of Ir(ppy)3 presented the highest current and power efficiencies, and the PVK based devices' electroluminescence spectrum showed an emission centered at 540 nm, suggesting that a charge unbalance and light emission from the injection layer of aluminum doped zinc oxide (AZO) occurred. Therefore, studies based on the PVK:AZO system and different PVK's average molar masses were elaborated to observe the PLEDs' electrical and optical properties. Results showed that AZO is a photo/electroluminescent material and it is responsible for the broad emission in the visible range. The hybrid device showed near pure white light emission and its purity reached 0.19.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2019-04-16
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.