Disertación de Maestría
DOI
10.11606/D.3.2016.tde-16062016-084316
Documento
Autor
Nombre completo
Bryane Prando Brandão
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2015
Director
Tribunal
Falleiros, Neusa Alonso (Presidente)
Magnabosco, Rodrigo
Ramirez, Mario Fernando Gonzalez
Título en portugués
Influência do tempo de imersão em solução aquosa contendo H2S  sobre a tenacidade de tubo API 5L X65 sour avaliada a partir de ensaio Charpy
Palabras clave en portugués
Ácido sulfídrico
Aço microligado
Ensaio Charpy
Fractografia
Fragilização por hidrogênio
Temperatura de transição.
Tenacidade dos materiais
Resumen en portugués
Com o decorrer dos anos o consumo de petróleo e seus derivados aumentou significativamente e com isso houve a necessidade de se investir em pesquisas para descobertas de novas jazidas de petróleo como o pré-sal. Porém, não apenas a localização dessas jazidas deve ser estudada, mas, também, sua forma de exploração. Essa exploração e extração, na maioria das vezes, se dão em ambientes altamente corrosivos e o transporte do produto extraído é realizado através de tubulações de aço de alta resistência e baixa liga (ARBL). Aços ARBL expostos a ambientes contendo H2S e CO2 (sour gas) sofrem corrosão generalizada que promovem a entrada de hidrogênio atômico no metal, podendo diminuir sua tenacidade e causar falha induzida pela presença de hidrogênio (Hydrogen Induced Cracking HIC), gerando falhas graves no material. Tais falhas podem ser desastrosas para o meio ambiente e para a sociedade. O objetivo deste trabalho é estudar a tenacidade, utilizando ensaio Charpy, de um tubo API 5L X65 sour após diferentes tempos de imersão em uma solução saturada com H2S. O eletrólito empregado foi a solução A (ácido acético contendo cloreto de sódio) da norma NACE TM0284 (2011), fazendo-se desaeração com injeção de N2, seguida de injeções de H2S. Os materiais foram submetidos a: ensaios de resistência a HIC segundo a norma NACE TM0284 (2011) e exames em microscópio óptico e eletrônico de varredura para caracterização microestrutural, de inclusões e trincas. As amostras foram submetidas a imersão em solução A durante 96h e 360h, sendo que, após doze dias do término da imersão, foram realizados os ensaios Charpy e exames fractográficos. Foram aplicados dois métodos: o de energia absorvida e o da expansão lateral, conforme recomendações da norma ASTM E23 (2012). As curvas obtidas, em função da temperatura de impacto, foram ajustadas pelo método da tangente hiperbólica. Esses procedimentos foram realizados nas duas seções do tubo (transversal e longitudinal) e permitiram a obtenção dos seguintes parâmetros: energias absorvidas e expansão lateral nos patamares superior e inferior e temperaturas de transição dúctil-frágil (TTDF) em suas diferentes definições, ou seja, TTDFEA, TTDFEA-DN, TTDFEA-FN, TTDFEL, TTDFEL-DN e TTDFEL-FN (identificação no item Lista de Abreviaturas e Siglas). No exame fractográfico observou-se que o material comportou-se conforme o previsto, ou seja, em temperaturas mais altas ocorreu fratura dúctil, em temperaturas próximas a TTDF obteve-se fratura mista e nas temperaturas mais baixas observou-se o aparecimento de fratura frágil. Os resultados mostraram que quanto maior o tempo de imersão na solução A, menor é a energia absorvida e a expansão lateral no patamar superior, o que pode ser explicado pelo (esperado) aumento do teor de hidrogênio em solução sólida com o tempo de imersão. Por sua vez, os resultados mostraram que há tendência à diminuição da temperatura de transição dúctil-frágil com o aumento do tempo de imersão, particularmente, as TTDFEA-DN e TTDFEL-DN das duas seções do tubo (longitudinal e transversal). Esse comportamento controverso, que pode ser denominado de tenacificação com o decorrer do tempo de imersão na solução A, foi explicado pelo aparecimento de trincas secundárias durante o impacto (Charpy). Isso indica uma limitação do ensaio Charpy para a avaliação precisa de materiais hidrogenados.
Título en inglés
Influence of immersion time in water solution containing H2S opn the toughness of pipe API 5L X65 Sour evaluated from Charpy test.
Palabras clave en inglés
Charpy impact test
HSLA steels
Hydrogen embrittlement
Hydrogen sulfide
Toughness
Transition temperature.
Resumen en inglés
Over the years the consumption of crude oil and its derivatives increased significantly, creating the necessity to invest in research to discover new sources of pre-salt crude oil. However, not only the location of these deposits should be studied, but also its extraction. This exploration and extraction, in most cases, occur in highly corrosive environments and the transport of the extracted product is performed by high strength low alloy steel pipes (HSLA). HSLA steels exposed to environments containing CO2 and H2S (sour gas) suffer general corrosion that promotes the diffusion of atomic hydrogen into the metal structure, which may decrease its toughness and induce cracks by the presence of hydrogen (Hydrogen Induced Cracking - HIC), leading the material to severe failures. Such events can be disastrous for the environment and the society. The objective of this work is to study the toughness using Charpy Impact Tests on an API 5L X65 sour service steel pipe, submitted to different immersion times in a H2S saturated solution. The used electrolyte was the NACE TM0284 (2011) solution A (acetic acid containing sodium chloride), with deaeration by N2 injection followed by H2S injection. The materials were submitted to HIC resistance tests according to NACE TM0284 (2011) standard and examination by optical microscopy and scanning electron microscopy for microstructural inclusions and cracks characterization. The samples were immersed in the solution for 96h and 360h and after twelve days of immersion, Charpy tests and fracture analysis were performed. Two analytical methods were applied to Charpy tests results: the energy absorbed and lateral expansion, as recommended by the ASTM E23 (2012). The obtained curves, that are a function of impact temperature, were adjusted by the hyperbolic tangent method. This procedure was performed in two different orientations in the pipe (transverse and longitudinal) and allowed the determination of the following parameters: energy absorbed and lateral expansion in the upper and lower levels and ductile-to-brittle transition temperatures (DBTT) in its different definitions: DBTTAE, DBTTAE-DN, DBTTAE-FN, DBTTLE, DBTTLE-DN e DBTTLE-FN. Fracture analysis revealed that the material behaved as expected, meaning that at higher temperatures ductile fracture occurred, at temperatures near DBTT it was obtained a mixed fracture and at lower temperatures it was observed the presence of brittle fracture. Results showed that when the immersion time in the solution was higher, the energy absorbed in upper shelf decreases, and also lateral expansion in upper shelf decreases, which may be explained by the (expected) increase of hydrogen level in solid solution, induced by the immersion time. It was found that there is a tendency of the ductile-to-brittle transition temperature to be lower with the increase of immersion time, particularly the DBTTAE-DN and DBTTLE-DN of the two pipe sections (longitudinal and transversal). This controversial behavior, which may be defined as the toughening by the increase of immersion time in the solution A, was explained by the appearance of secondary cracks during impact test (Charpy). This indicates a limitation of the Charpy test for the accurate characterization of hydrogenated materials, concerning toughness.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-06-17
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • BRANDAO, B. P., et al. Microstructures of API 5L X65 pipeline HIC resistance. In Rio pipeline conference and exposition 2013, Rio de Janeiro, 2013. Rio pipeline conference and exposition 2013-Technical Papers.Rio de Janeiro : IBP, 2013.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.