Master's Dissertation
DOI
10.11606/D.3.2013.tde-17102014-120751
Document
Author
Full name
Alan Barros de Almeida
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2013
Supervisor
Committee
Landgraf, Fernando José Gomes (President)
Goldenstein, Hélio
Magnabosco, Rodrigo
Title in Portuguese
Detecção da transformação da austenita retida por deformação plástica em aços para gasodutos classe API 5L X80 através de medidas magnéticas.
Keywords in Portuguese
Aço ARBL API X80
Austenita retida
Densidade de massa
Difração de raios X
Polarização magnética
Transformação martensítica induzida por deformação
Abstract in Portuguese
O presente trabalho avaliou o efeito de tratamentos térmicos ou diferentes graus de deformação plástica na transformação da austenita do microconstituinte AM de uma chapa de aço alta resistência baixa liga (ARBL) classe API 5L X80 usada para gasodutos. A chapa tem espessura de 19 mm e passaria pelo processo de conformação UOE, mas a deformação foi realizada por laminação a frio, a temperatura ambiente, com reduções de 5 a 20%. O propósito foi compreender melhor o microconstituinte AM, explorar a transformação martensítica induzida por deformação (SIMT) e a decomposição austenítica por tratamento térmico, com ênfase em seu comportamento magnético. A transformação da austenita foi acompanhada através de medidas de polarização magnética, comparada com a densidade de massa e difração de raios X. A deformação plástica e os tratamentos térmicos alteraram a polarização magnética de saturação e a densidade de massa da amostra de aço de forma compatível com a eliminação da austenita retida metaestável. O método de densidade hidrostática foi considerado sensível para mensurar transformações de fase. Os dados obtidos revelam expansão volumétrica de aproximadamente 0,13%, correspondendo a 3,2% a quantidade de austenita retida original do material, enquanto os valores obtidos por polarização magnética de saturação são 2,8% pelo histeresígrafo e 2,1% por MAV. A difração de raios X nas amostras sob deformação ou tratamentos térmicos resultaram em queda nos primeiros picos da austenita quando comparadas com a amostra como recebida.
Title in English
Detecting austenite transformation by plastic deformation in grade API 5L X80 pipeline steel by magnetic properties.
Keywords in English
HSLA steels API X80
Mass density
Retained austenite
Saturation magnetization
Strain-induced martensitic transformation
X ray diffraction
Abstract in English
This study evaluated the effect of different degrees of plastic deformation or heat treatment on the transformation of austenite into martensite of an HSLA steel plate API 5L X80 for pipelines. A 19 mm thickness plate would be submitted to UOE forming process, but the cold work instead occurred by cold rolling at room temperature, with reductions of 5 up to 20%. The purpose was to better understand the MA constituent, explore the strain-induced martensitic transformation (SIMT) and austenitic decomposition by heat treatment with emphasis on its magnetic behavior. The transformation was accompanied by saturation magnetization measurements, compared with the mass density and X-ray diffraction. The plastic deformation or the heat treatment altered the saturation magnetization and the mass density in a manner consistent with the elimination of metastable retained austenite. The density method is sensible to measure phase transformations induced by strain. The data obtained shows a volumetric expansion of about 0.13%, corresponding to an amount of retained austenite of the original material of 3.2%, while the values obtained by magnetization saturation are 2.8% by hysteresigraph and 2.1% by VSM. By X-ray diffraction there is a clear drop in first peaks of austenite of the samples under deformation or heat treatment compared with the sample as-received.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2014-10-22
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.