Mémoire de Maîtrise
DOI
10.11606/D.3.2013.tde-17102014-120751
Document
Auteur
Nom complet
Alan Barros de Almeida
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2013
Directeur
Jury
Landgraf, Fernando José Gomes (Président)
Goldenstein, Hélio
Magnabosco, Rodrigo
Titre en portugais
Detecção da transformação da austenita retida por deformação plástica em aços para gasodutos classe API 5L X80 através de medidas magnéticas.
Mots-clés en portugais
Aço ARBL API X80
Austenita retida
Densidade de massa
Difração de raios X
Polarização magnética
Transformação martensítica induzida por deformação
Resumé en portugais
O presente trabalho avaliou o efeito de tratamentos térmicos ou diferentes graus de deformação plástica na transformação da austenita do microconstituinte AM de uma chapa de aço alta resistência baixa liga (ARBL) classe API 5L X80 usada para gasodutos. A chapa tem espessura de 19 mm e passaria pelo processo de conformação UOE, mas a deformação foi realizada por laminação a frio, a temperatura ambiente, com reduções de 5 a 20%. O propósito foi compreender melhor o microconstituinte AM, explorar a transformação martensítica induzida por deformação (SIMT) e a decomposição austenítica por tratamento térmico, com ênfase em seu comportamento magnético. A transformação da austenita foi acompanhada através de medidas de polarização magnética, comparada com a densidade de massa e difração de raios X. A deformação plástica e os tratamentos térmicos alteraram a polarização magnética de saturação e a densidade de massa da amostra de aço de forma compatível com a eliminação da austenita retida metaestável. O método de densidade hidrostática foi considerado sensível para mensurar transformações de fase. Os dados obtidos revelam expansão volumétrica de aproximadamente 0,13%, correspondendo a 3,2% a quantidade de austenita retida original do material, enquanto os valores obtidos por polarização magnética de saturação são 2,8% pelo histeresígrafo e 2,1% por MAV. A difração de raios X nas amostras sob deformação ou tratamentos térmicos resultaram em queda nos primeiros picos da austenita quando comparadas com a amostra como recebida.
Titre en anglais
Detecting austenite transformation by plastic deformation in grade API 5L X80 pipeline steel by magnetic properties.
Mots-clés en anglais
HSLA steels API X80
Mass density
Retained austenite
Saturation magnetization
Strain-induced martensitic transformation
X ray diffraction
Resumé en anglais
This study evaluated the effect of different degrees of plastic deformation or heat treatment on the transformation of austenite into martensite of an HSLA steel plate API 5L X80 for pipelines. A 19 mm thickness plate would be submitted to UOE forming process, but the cold work instead occurred by cold rolling at room temperature, with reductions of 5 up to 20%. The purpose was to better understand the MA constituent, explore the strain-induced martensitic transformation (SIMT) and austenitic decomposition by heat treatment with emphasis on its magnetic behavior. The transformation was accompanied by saturation magnetization measurements, compared with the mass density and X-ray diffraction. The plastic deformation or the heat treatment altered the saturation magnetization and the mass density in a manner consistent with the elimination of metastable retained austenite. The density method is sensible to measure phase transformations induced by strain. The data obtained shows a volumetric expansion of about 0.13%, corresponding to an amount of retained austenite of the original material of 3.2%, while the values obtained by magnetization saturation are 2.8% by hysteresigraph and 2.1% by VSM. By X-ray diffraction there is a clear drop in first peaks of austenite of the samples under deformation or heat treatment compared with the sample as-received.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2014-10-22
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.