Mémoire de Maîtrise
DOI
10.11606/D.3.2013.tde-26062014-162610
Document
Auteur
Nom complet
Diego Martins Garcia
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2013
Directeur
Jury
Brandi, Sérgio Duarte (Président)
Dalpiaz, Giovani
Eckstein, Carlos Bruno
Titre en portugais
Influência dos parâmetros de soldagem na resistência à fluência de juntas soldadas de aço  ASTM A 335 P91.
Mots-clés en portugais
Aço P91
Arame tubular
Fluência
Soldagem
Resumé en portugais
A utilização do aço ASTM A 335 P91 tem sofrido um aumento considerável, especialmente em função da necessidade de materiais com maior resistência à fluência para aplicações em unidades de utilidades (geração de vapor) e de processo. Por ser um material de difícil soldabilidade, diversos problemas são enfrentados durante a construção das unidades e, posteriormente, durante manutenção, geralmente em função de problemas de soldagem oriundos da fase de fabricação e construção. As normas de projeto e construção utilizadas internacionalmente vêm sofrendo adaptações a fim de melhorar a utilização deste material, mas seus requisitos ainda apresentam importantes lacunas em relação às principais práticas recomendadas pela literatura técnica mais atual. Visando uma melhor utilização deste material, obtendo juntas soldadas com propriedades mecânicas e metalúrgicas mais consistentes, o presente trabalho foi desenvolvido avaliando-se a influência de parâmetros de soldagem energia de soldagem e temperatura de tratamento térmico pós-soldagem (TTPS) sobre as propriedades mecânicas e metalúrgicas, incluindo resistência à fluência, de juntas soldadas de aço ASTM A 335 P91. Foram testadas nove juntas soldadas, combinando três níveis de energia de soldagem com três temperaturas de TTPS. Os resultados obtidos indicam que é possível ter melhor controle sobre as propriedades deste material, desde que se opere com níveis mais restritos de energia de soldagem e maiores temperatura de TTPS, observando-se as limitações pertinentes, especialmente no que tange à temperatura crítica de transformação Ac1.
Titre en anglais
Influence of welding parameters on creep resistance of ASTM A 335 P91 steel welded joint.
Mots-clés en anglais
Creep
Fluency
Flux cored arc welding
Steel P91
Welding
Resumé en anglais
The use of ASTM A 335 P91 has been increased considerably specially because of the need for materials with higher creep resistance for power generation (nuclear and thermoelectric) and oil and gas processing applications. As this is a material with poor weldability, several issues are faced during construction of these unities, and later during maintenance usually associated with welding problems originated in the fabrication and construction phase. The design and construction codes most used worldwide are receiving important revisions targeting to enhance the use condition of this material but its requirements still show important lacks when compared to the main practices recommended by the more recent technical literature. Aiming a better usage of this material obtaining sound welded joints with more consistent metallurgical and mechanical properties, this work was developed assessing the influence of some welding parameters welding heat input and temperature of post-­weld heat treatment (PWHT) on the metallurgical and mechanical properties, including creep strength, of welded joints of ASTM A 335 P91 steel. Nine welded joints were submitted to testing, combining three different levels of welding heat input with three different PWHT temperatures. The results show that it is possible to have a better control over the properties of this material since it is used lower welding heat inputs combined to higher PWHT temperatures, taking care about the limitations regarding the critical transformation temperature Ac1.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2014-07-02
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.