Mémoire de Maîtrise
DOI
10.11606/D.3.2017.tde-26092017-142318
Document
Auteur
Nom complet
Kimie Ino
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2017
Directeur
Jury
Gouvea, Douglas (Président)
Menegazzo, Ana Paula Margarido
Pileggi, Rafael Giuliano
Titre en portugais
Estudo da reologia de uma massa de porcelana fosfática para uso na conformação em torno elétrico.
Mots-clés en portugais
Bentonita
Plasticidade
Porcelana
Reologia
Torno elétrico
Resumé en portugais
A conformação em torno elétrico é um dos métodos utilizados na fabricação de peças cerâmicas, principalmente utilitários e decorações. Porém nem todas as massas cerâmicas possuem plasticidade adequada para serem torneadas. A porcelana fosfática é um desses exemplos devido à composição de 50 % de cinza de ossos bovinos, 25 % de caulim e 25 % de feldspato. Uma massa de porcelana comercial de alta temperatura, branca e com boa plasticidade foi a referência de massa propícia para se trabalhar no torno elétrico e foi feito a caracterização desse material como distribuição granulométrica, picnometria a gás, composição química por fluorescência de raio X (FRX) e difração de raio X (DRX). Os mesmos métodos de caracterização foram feitos na porcelana fosfática. O limite de Atterberg foi utilizado como técnica para medir os teores de água das massas e a reometria por squeeze flow foi o método de análise para diferenciar massas cerâmicas plásticas e não-plásticas. Testes no torno elétrico foram feitos para concluir sobre melhoria na plasticidade da porcelana fosfática através da adição de aditivo como bentonita e polímero à base de éter celulose (MHEC). Adição de 4 % de bentonita na porcelana fosfática aumentou o índice de plasticidade de Atterberg em cerca de 100 % e as curvas de squeeze flow ficaram próximos das curvas do material de referência, apresentando assim plasticidade suficiente para fabricar peças no torno elétrico.
Titre en anglais
Phosphatic porcelain for forming by throwing wheel: a study of rheology.
Mots-clés en anglais
Bentonite
Phosphatic porcelain
Plasticity
Squeeze flow
Throwing wheel
Resumé en anglais
Throwing on electric wheel is one of techniques used to forming ceramic wares as tableware and decorative. However, ceramic body needs to have enough plasticity for hands working on throwing wheel. The phosphatic porcelain composition is 50 % of bone ash, 25 % of kaolin and 25 % of feldspar and generally has low plasticity. A commercial porcelain for throwing on the electric wheel was used as default and compared with the phosphatic porcelain. Raw material characterization as particle size distribution analysis, gas pycnometry, chemical composition by x-ray fluorescence (XRF), zeta potential and x-ray diffraction (XRD) was doing to compare both porcelains. Atterberg limits were used to measure moisture content of ceramic body and rheometry was evaluated by squeeze flow technique to determine the viscosity difference between porcelain and phosphatic porcelain. Test on the throwing wheel were made to verify plasticity improvement by addition of bentonite or a polymer based on ether cellulose (MHEC). The 4 % of bentonite addition increased about 100 % the Atterberg limit and the consequent change in the squeeze flow curves demonstrate to be similar with reference and with enough plasticity to throwing on the electric wheel. Keyword: Phosphatic porcelain. Plasticity. Throwing wheel. Bentonite. Squeeze flow.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
KimieInoCorr17.pdf (4.81 Mbytes)
Date de Publication
2017-09-29
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.