• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.3.1997.tde-27072001-165148
Documento
Autor
Nombre completo
Antonio José Ramirez Londoño
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1997
Director
Tribunal
Brandi, Sergio Duarte (Presidente)
Pope, Alexandre Meirelles
Taniguchi, Celio
Título en portugués
Estudo da precipitação de nitreto de cromo e fase sigma por simulação térmica da zona afetada pelo calor na soldagem multipasse de aços inoxidáveis duplex.
Palabras clave en portugués
fase sigma
nitreto de cromo
precipitação de fases intermetálicas
soldagem de aços inoxidáveis duplex
Resumen en portugués
Os aços inoxidáveis duplex são materiais com um excelente desempenho, devido às suas sobressalentes propriedades mecânicas e excelente resistência à corrosão. Uma composição química adequada e microestrutura balanceada são as responsáveis por esta combinação de propriedades. No entanto, são estes mesmos fatores que os fazem especialmente susceptíveis à precipitação de fases intermetálicas, com efeitos maléficos no seu desempenho. Durante os ciclos térmicos de uma soldagem multipasse, a precipitação de intermetálicos é crítica. Foi desenvolvido um método para simular os ciclos térmicos de uma solda multipasse. Usando este método, foi estudada a precipitação de nitreto de cromo e fase sigma na zona afetada pelo calor submetida a temperaturas abaixo de 950°C dos aços inoxidáveis duplex UNS S31803 e S32550. Foram estudadas energias de soldagem na faixa de 0,4 a 1,0 kJ/mm. Foi determinada mediante extração de precipitados, seguida de difração de raios X na câmara de Debye-Scherrer e microscopia eletrônica de transmissão, a precipitação de nitreto de cromo para energias de soldagem de 0,4 a 1,0 kJ/mm e de fase sigma para energias de soldagem de 0,6-1,0 KJ/mm, no UNS S32550. Já o UNS S31803 não apresentou precipitação alguma para as energias de soldagem estudadas. Baseando-se nos resultados verifica-se que durante uma soldagem multipasse o UNS S31803 é menos propenso que o UNS S32550 à precipitação de intermetálicos na zona afetada pelo calor submetida a temperaturas abaixo de 950°C.
Título en inglés
Chromium nitride and sigma phase precipitation study by heat-affected zone thermal simulation of duplex stainless steels multipass welding.
Palabras clave en inglés
chromium nitride
duplex stainless steels welding
intermetallic phases precipitation
sigma phase
Resumen en inglés
Duplex stainless steels belong to a group of high performance stainless steels regarding to corrosion and mechanical properties. These achievements are related to a suitable chemical composition and a balanced microstructure. During welding thermal cycles the microstructure changes and, consequently, corrosion and mechanical properties might be impaired due to a precipitation of intermetallic phases. This precipitation is an issue to be addressed for multipass welding. It was developed a method for simulate the multipass welding thermal cycles. Using this method chromium nitride and sigma phase precipitation was studied in a simulated heat affected zone of multipass welding (three passes) of UNS S31803 and UNS S32550 duplex stainless steels with different heat inputs (0,4 to 1,0 kJ/mm). The HAZ simulated region was below 950°C maximum temperature. Microstructural characterization of simulated samples showed discontinuous films of a precipitated phase at ferrite/ferrite grain boundaries and ferrite/austenite interfaces were observed only in a UNS S32550 duplex grade for all heat inputs simulated. This suggests that sigma phase and chromium nitride precipitation took place during sample thermocycling. X-ray diffraction in a Debye-Scherrer chamber of extracted precipitates and electron diffraction by TEM confirmed the presence of chromium nitrides for all range of heat input studied and sigma phase for heat input above 0,6 kJ/mm. On the other hand, microstructural analysis of UNS S31803 simulated samples did not present precipitation of intermetallic phases in the tested temperature range of HAZ. Based on these results, UNS S31803 is more resistant than UNS S32550 to intermetallic phases precipitation in multipass welding.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Antonio-Ramirez.pdf (3.52 Mbytes)
Fecha de Publicación
2001-08-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.