• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Tesis Doctoral
DOI
10.11606/T.3.2017.tde-27072017-104746
Documento
Autor
Nombre completo
Helio Goldenstein
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1984
Director
Tribunal
Falleiros, Ivan Gilberto Sandoval (Presidente)
Padilha, Angelo Fernando
Qualifik, Paul
Silva, Paulo Sergio Carvalho Pereira da
Título en portugués
Crescimento competitivo de precipitados .. em cobre-alumínio.
Palabras clave en portugués
Bronze de alumínio
Materiais
Maturação de Ostwald em precipitados coerentes
Resumen en portugués
Estudou-se a evolução morfológica de precipitados .. em matriz .. Cu-Al, através de tratamentos isotérmicos interrompidos por têmpera, em amostras previamente solubilizadas desde o início da precipitação, até o crescimento competitivo. Caracterizou-se a forma dos precipitados após tratamentos em diversas temperaturas, por microscopia ótica e microscopia eletrônica de varredura, de estruturas atacadas profundamente. A forma dos precipitados após tratamentos prolongados a 700 ºC tende a ser esférica, enquanto nos tratamentos a 600 ºC, tende a ser facetada. Com temperaturas decrescentes de 700 º para 600 ºC a forma passa gradualmente de esférica para facetada. Verificou-se que a distribuição espacial dos precipitados depende da velocidade de aquecimento. Com altas velocidades (tratamento em banho de sal), a distribuição é homogênea; com velocidade de aquecimento lentas (tratamento em forno de mufla) os precipitados apresentam-se alinhados, indicando nucleação heterogênea. O crescimento competitivo foi caracterizado através de medidas das distribuições de tamanhos de precipitados. Esta medida foi realizada utilizando micrografias de secções polidas, com um equipamento semi-automático. As medidas de distribuição de tamanhos das secções de precipitados foram processadas para a obtenção da distribuição de diâmetros reais dos precipitados através de um programa de computador utilizando o algoritmo de Saltykov. .........
Título en inglés
Competitive growth of .. precipitates in .. cobre-alumínio.
Palabras clave en inglés
Aluminum bronzes
Competitive growth
Ostwald ripening
Resumen en inglés
The morphological evoluation of .. precipitates in a . Cu-Al matrix has been studied from the beginning of precipitation until coarsening, using isothermal treatments on previously solubilized samples. The shape of precipitates after treatments at many temperatures was studied using Optical Microscopy and Scanning Electron Microscopy of deep etched samples. The precipitates treated for long periods at 700 ºC approach an spherical shape, while treatments at 600 ºC the precipitates become faceted. The special distribution of the precipitates are determined by the heating rate from room temperature to isothermal treatment temperature. With high heating rates the distribution is homogeneous. With low heating rate the precipitates are arranged in rows, due to heterogeneous nucleation. Coarsening was studies by measuring the distribution of precipitate sizes on microphotographs of polished sections using a semi-automatic device. The mesures of section sizes were processed to obtain the real diameter distribution using a computer program based on Saltykov's algoritm. .....
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-07-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.