Tesis Doctoral
DOI
10.11606/T.3.2009.tde-28052009-141416
Documento
Autor
Nombre completo
Silvio Luiz Miranda Brito
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Gouvêa, Douglas (Presidente)
Bertochi, Maria Aparecida Zaghete
Muccillo, Eliana Navarro dos Santos
Ortega, Fernando dos Santos
Pileggi, Rafael Giuliano
Título en portugués
Síntese, caracterização e modificação superficial de nano partículas de titanato de bário produzidas pelo método Pechini.
Palabras clave en portugués
Formação de fase
Modificação de superfície
Pechini
Titanato de bário
Resumen en portugués
A síntese de nano partículas e a sua caracterização tem sido a grande mola propulsora do desenvolvimento de materiais nano-estruturados. Pouca atenção tem sido dedicada aos fenômenos físico-químicos relacionados às enormes superfícies intrínsecas destes materiais. Dentre eles, o titanato de bário ocupa uma posição de destaque devido ao seu grande potencial na geração de produtos de alta tecnologia. Neste estudo o BaTiO3 foi sintetizado pelo método Pechini que proporciona a geração de nanopartículas de grande uniformidade química. Contudo, o uso de cátions que formam carbonatos de alta estabilidade pode inviabilizar o uso do método. Os pós de titanato de bário preparados apresentaram elevada área de superfície específica, mas formação de fases parasitas de carbonato de bário e em algumas estequiometrias de ortotitanato de bário e carbonatos adsorvidos à superfície do titanato de bário. O estudo sistemático da química de superfície e da estrutura cristalina do material permitiu a proposta de um método de lixiviação em meio ácido onde as fases parasitas foram eliminadas e um material nanométrico de grande potencial de aplicação foi obtido com as seguintes características: fase com simetria tetragonal predominante ~95% (apesar da coexistência de fase cúbica ~5%); tamanho de cristalito ou partícula primária de 44 nm; área de superfície específica igual a 13,4 m2/g e D(BET) de 74 nm; está isento de contaminação de carbonatos ou outra fase; relação estequiométrica de Ba/Ti = 0,96 -> Ba0,98Ti1,02O3.
Título en inglés
Synthesis, characterization and surface modification in barium titanate nano particles by Pechini method.
Palabras clave en inglés
Barium titanate
Pechini
Phase forming
Surface modification
Resumen en inglés
The synthesis and characterization of Nanoparticles has been a great topic for nanostructured materials developments. The Relationship between Physicochemical phenomena and large surface area has had a little attention. The barium titanate has a great potential of high-tech products generation. In this work, the BaTiO3 was prepared by polymeric precursor method because this method generates a great chemical uniformity in nanoparticles. However, cations that form carbonates of high-stability may compromise this method use. The barium titanate powder was prepared and showed high specific surface area, but this powder has barium carbonate and ortotitanato contamination. The systematic surface chemistry and crystal structure study suggest an acid leaching method to contaminant phases eliminated. A nanomaterial of great potential for application was obtained with the following characteristics: tetragonal phase predominant ~95% (cubic phase coexist ~5%); crystallite size of 44 nm; surface area of 13,4 m2/g and Particle size (estimated BET) of 74 nm; carbonate free; Ba/Ti = 0,96 -> Ba0,98Ti1,02O3.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-07-03
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.