Disertación de Maestría
DOI
10.11606/D.3.2002.tde-29072003-144316
Documento
Autor
Nombre completo
Eduardo Franco de Monlevade
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2002
Director
Tribunal
Falleiros, Ivan Gilberto Sandoval (Presidente)
Ferrante, Maurizio
Tschiptschin, Andre Paulo
Título en portugués
Relações de orientação resultantes da precipitação de austenita em ferrita em aço inoxidável dúplex.
Palabras clave en portugués
aços inoxidáveis dúplex
EBSD
relações de orientação
Resumen en portugués
Aços inoxidáveis dúplex apresentam uma estrutura composta por ferrita e austenita. O fato de a austenita ser estável à temperatura ambiente possibilita que esses aços sejam usados no estudo da reação de formação da austenita a partir da ferrita, podendo os resultados ser aplicados a aços de baixa liga, em que a austenita se transforma em martensita no resfriamento brusco, e a outros sistemas com transformações entre fases cúbicas de corpo centrado (CCC) e cúbicas de face centrada (CFC). Foram realizados estudos em um aço inoxidável dúplex do tipo DIN W.Nr. 1.4462 (UNS 31803). As amostras foram solubilizadas no campo ferrítico a 1325°C e resfriadas em água. As amostras foram ainda tratadas isotermicamente em temperaturas entre 700°C e 1100°C por tempos entre 5.000 e 30.000 segundos. Deste modo, a formação de austenita a partir da ferrita foi estudada em seu estágio inicial e em estágios avançados da reação, com relação aos seus aspectos morfológicos e cristalográficos. As morfologias encontradas apresentaram variações dependentes dos segmentos de contorno de grão em que as partículas se formam. As partículas nucleadas nos contornos de grão podem ser adequadamente descritas pela classificação morfológica de Dubé. Além disso, essas partículas apresentaram, em geral, relações de orientação do tipo Kurdjumov-Sachs e Nishyiama-Wassermann com pelo menos um dos dois grãos, podendo ser encontradas relações intermediárias entre essas duas. . Em alguns casos, as partículas mantêm relações de orientação com os dois grãos adjacentes, apresentando pequenos desvios das relações exatas relatadas na literatura. As partículas de austenita intragranulares apresentam desvios em relação à relações exatas maiores do que os encontrados nas partículas de contornos de grão. Em alguns casos, as partículas intragranulares aparentam não apresentar relações de orientação com a matriz ferrítica.
Título en inglés
Orientation relationships resulting from austenite formation from ferrite in duplex stainless steel.
Palabras clave en inglés
duplex stainless steels
EBSD
orientation relationships
Resumen en inglés
Duplex Stainless Steels have a structure composed by ferrite and austenite. The fact that austenite, in these steels, is stable at low temperatures, allows the use of these steels in studies of austenite formation from ferrite, in such way that the results can be applied to low alloy steels, in which austenite transforms to martensite upon rapid cooling, and to other systems containing transformations between body-centred cubic (BCC) and face-centred cubic (FCC) phases. Studies were performed on a DIN W.Nr. 1.4462 (UNS 31803) duplex stainless steel. The samples were solution treated in the ferrite region at 1325°C and water cooled. Samples were then submitted to isothermal treatments at temperatures between 700°C and 1100°C for up to 30.000 seconds. In this way, austenite formation from ferrite was studied on initial and advanced stages of the reaction, concerning morphological and crystallographic aspects. The morphologies observed varied with the grain boundary segment in which the particles were formed. The grain boundary particles may be adequately described by the Dubé classification. Moreover, these particles presented Kurdjumov-Sachs and Nishyiama-Wassermann orientation relationships with at least one of the adjacent grains, with possibilities of occurrence of intermediate relationships between K-S and N-W relationships. In some cases, the particles show orientation relationships with both adjacent grains, with small deviations form the exact relationships reported in literature. Intragranular austenite particles show higher deviations from the exact relationships than grain boundary particles. In some cases, intragranular particles have no apparent orientation relationships with the ferrite matrix.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
OR_Acos_duplex.pdf (6.30 Mbytes)
Fecha de Publicación
2003-08-12
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • MONLEVADE, E. F., and FALLEIROS, I. G. S.. Orientation relationships associated with austenite formation from ferrite in a coarse-grained duplex stainless steel [doi:10.1007/s11661-006-0067-1]. Metallurgical and Materials Transactions A [online], 2006, vol. 37, n. 3, p. 939-949.
  • MONLEVADE, Eduardo Franco, GOLDENSTEIN, Helio, and FALLEIROS, Ivan Gilberto Sandoval. Intragranular formation of austenite during delta ferrite decomposition in a duplex stainless steel [doi:10.1007/s10853-010-4468-6]. Journal of Materials Science [online], 2010, vol. 45, n. 18, p. 5089-5093.