Tesis Doctoral
DOI
10.11606/T.3.2009.tde-29092010-164518
Documento
Autor
Nombre completo
Patricia Schmid Calvão
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Demarquette, Nicole Raymonde (Presidente)
Carvalho, Laura Hecker de
Cavaille, Jean Yves
Gauthier, Catherine
Soldi, Valdir
Título en portugués
Obtenção e caracterização de misturas do polímero biodegradável P[3HB] e seu copolímero P[3HB-co-3HV] com elastômeros.
Palabras clave en portugués
Biomateriais (processamento)
Blendas
Elastômeros
Resumen en portugués
Neste trabalho foi desenvolvido um estudo com o poliéster biodegradável P[3HB] (poli[R-3-hidroxibutirato]) e seu copolímero P[3HB-co-3HV] (poli[R-3-hidroxibutirato-co-3- hidroxivalerato]). Esses materiais são conhecidos por seu grande potencial de biodegradabilidade, porém sua utilização pela indústria ainda é limitada em função de seu baixo desempenho mecânico. Visando a tenacificação desses materiais, optou-se por misturá-los com os elastômeros EPDM (terpolímero de etileno-propileno-dieno) e PVB (Poli(vinil butiral)). Foram estudados quatro grupos de blendas: P[3HB]/EPDM e P[3HB-co- 3HV]/EPDM processados em misturadores internos e posteriormente prensadas em filmes; P[3HB]/EPDM e P[3HB]/PVB extrudados e posteriormente injetados. As blendas foram obtidas nas concentrações de 10, 20 e 30% em peso de elastômeros. Inicialmente, estudou-se efeito da incorporação de elastômeros na cristalinidade, estrutura cristalina, propriedades térmicas e dinâmico-mecânicas das matrizes, e o efeito do tipo de processamento utilizado. Observou-se que a adição dos elastômeros às matrizes semicristalinas aumentou a nucleação de esferulitos, resultando em um aumento da cristalinidade das mesmas. O PVB apresentou um efeito plastificante na estrutura do PHB. Os filmes apresentaram uma degradação térmica maior que as amostras injetadas, resultando em uma cristalização mais lenta e um grau de cristalinidade maior. Em um outro estudo, avaliou-se a morfologia, tensão interfacial, comportamento reológico, propriedades mecânicas e a biodegradabilidade das amostras estudadas. Foi observada uma morfologia de dispersão de gotas para todas as misturas, exceto para a mistura P[3HB]/EPDM obtida por injeção que apresentou um certo grau de co-continuidade. No caso das misturas injetadas foi visto que o fator que parece influenciar mais fortemente em sua morfologia final são as razões de viscosidade observadas entre a matriz e a fase dispersa das mesmas. A adição de elastômeros aumentou a resistência ao impacto do P[3HB], principalmente no caso da mistura P[3HB]/EPDM, o que pode estar relacionado à morfologia co-contínua observada nesta blenda. A incorporação dos elastômeros resultou em uma redução do módulo de elasticidade e da resistência à tração do P[3HB], e aumento do alongamento, principalmente no caso da mistura com PVB. Foi visto que a biodegradação do P[3HB] e P[3HB-co-3HV] aumentou com a adição de elastômeros, devido à morfologia de dispersão e a diminuição do tamanho dos esferulitos que aumentam a área interfacial para a ação das enzimas, facilitando a biodegradação.
Título en inglés
Obtention and characterization of polymer blends based on P[3HB] and its copolymer P[3HB-co-3HV] with elastomers.
Palabras clave en inglés
Biomaterials
Blends
Elastomers
Resumen en inglés
In this work a study with the biodegradable polyester P[3HB] (poly[R-3- hydroxybutyrate]) and its copolymer P[3HB-co-3HV] (poly[R-3-hydroxybutyrate-co-3- hydroxyvalerate]) was conducted. These materials are known for their high biodegradability but their use is still limited because of their poor mechanical properties. In order to improve these properties it was chosen to blend these biodegradable polymers with EPDM (Ethylene propylene diene monomer) and PVB (Polyvinyl butyral). Four groups of blends were obtained: P[3HB]/EPDM and P[3HB-co-3HV]/EPDM blends were prepared using an internal mixer and then compressed molded; P[3HB]/PVB and P[3HB]/EPDM blends were prepared using an extruder and further injected. The blend concentrations ranged from 10 to 30 wt. % of the rubbery phase. Initially, the effect of rubber type on the crystallinity, the crystalline structure, thermal and dynamic-mechanical properties of the matrices and the effect of processing method to obtain the blends were investigated. The addition of elastomers on P[3HB] (and P[3HB-co- 3HV]) increases the nucleation, resulting in an increase of matrix crystallinity. PVB showed a plasticizing effect on the P[3HB] structure. Film samples showed a higher thermal degradation than injected ones, resulting in a slower crystallization and higher crystallinity. The morphology, interfacial tension, rheological behavior, mechanical properties (tensile and impact) and biodegradability of samples were also studied. A droplet dispersion morphology type was obtained for all the blends except for P[3HB]/EPDM injected samples which presented some extent of degree of continuity. The experimental results indicated that the final morphology observed for the blends was controlled by the viscosity ratio between the matrix and dispersed phase. Elastomer addition increased P[3HB] impact strength mainly for P[3HB]/EPDM blends, probably due to its co-continuous morphology. Moreover, elastomer incorporation resulted in a decrease of P[3HB] elastic moduli and tensile strength and increase of elongation of break, mainly for P[3HB]/PVB blends. It was observed that P[3HB] and P[3HB-co-3HV] biodegradation increased with elastomer addition due to the droplet dispersion morphology and decrease of spherulites size witch causes an increase of interfacial area for enzymes, facilitating biodegradation.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-10-05
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.