Disertación de Maestría
DOI
10.11606/D.3.2019.tde-30012019-091915
Documento
Autor
Nombre completo
Izabela Ferreira Girão
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2018
Director
Tribunal
Goldenstein, Helio (Presidente)
Payão Filho, João da Cruz
Vilarinho, Louriel Oliveira
Título en portugués
Estudo do efeito do aporte térmico de uma solda SAW na zona afetada pelo calor de um material API 5L X100M através de simulações computacionais.
Palabras clave en portugués
Aço
Resistência dos materiais
Soldagem
Tenacidade dos materiais
Resumen en portugués
Este trabalho tem por objetivo simular a zona de grãos grosseiros da ZAC através da simulação computacional em software de elementos finitos e submeter amostras de um aço microligado API 5L X100M a ciclagens térmicas na Gleeble para representar a região de estudo e, dessa forma, caracterizar e comparar o comportamento mecânico e microestrutural do material frente a diferentes aportes térmicos. Foram realizadas simulações de soldagem por arco submerso (SAW) em software computacional de elementos finitos para os aportes térmicos 2.0, 2.5, 3.0, 3.5, 4.0, 4.5 e 5.0 kJ/mm e obtidos os ciclos térmicos de um local correspondente à zona de grãos grosseiros da zona afetada pelo calor (ZAC). Em seguida, o ciclo obtido para cada aporte simulado foi utilizado como fonte para a simulação térmica na Gleeble de amostras do metal de base de um tubo produzido para a norma API 5L grau X100M. Em seguida, foram realizados ensaios de microdureza nos corpos de prova após simulações térmicas na Gleeble e no material de base como recebido, para efeitos de comparação dos resultados. Para cada aporte de calor simulado, um corpo de prova foi destinado para avaliação de microdureza e posterior análise microestrutural. As amostras remanescentes foram submetidas a ensaio de impacto charpy em temperatura de 0°C para as amostras de aporte de calor 2.5, 3.0, 4.0 e 4.5 kJ/mm e, para os demais aportes térmicos foi feito levantamento de curva de transição entre as temperaturas de -60 a 24°C. Os resultados obtidos demonstraram que existe uma correlação entre tenacidade, aporte de calor e morfologia do constituinte MA gerado na região de estudo, de maneira que foram obtidos menores valores de energia absorvida conforme maior o aporte de calor simulado. Também, nessas condições foi observado que o constituinte MA apresentou uma maior tendência ao formato globular que ao alongado.
Título en inglés
Effect of the heat input of an SAW welding in the heat affected zone of an API 5L X100M steel through computational simulations.
Palabras clave en inglés
API 5L X100M steel
Coarse grain region
Finite element analysis
MA constituent
Submerged arc welding
Thermal simulation
Resumen en inglés
The objective of this study is to simulate the coarse grain from the heat affected zone (CGHAZ) through computer simulation in finite element software and to submit samples of an API 5L X100M micro alloyed steel to thermal cycling in Gleeble to replicate this region and thus characterize and compare the mechanical and microstructural behavior of the material face to different heat inputs. Submerged Arc Welding (SAW) simulations were performed in finite elements software for heat inputs of 2.0, 2.5, 3.0, 3.5, 4.0, 4.5 and 5.0 kJ/mm. Afterwards, the thermal cycle curve obtained for each simulated heat input was used as the source for the thermal simulation in Gleeble of samples taken from the base metal of a pipe produced for API 5L standard and X100M grade. Subsequently, microhardness tests were performed in the Gleeble simulated samples and in as received material for the purpose of comparing the results. For each heat input simulated, one test specimen was used for microhardness and microstructural analysis. The remaining samples were subjected to a charpy V notch impact test at the temperature of 0°C for the 2.5, 3.0, 4.0 e 4.5 kJ/mm heat inputs and a transition curve was plotted between -60 up to 24°C for heat inputs 2.0, 3.5 and 5.0 kJ/mm. The obtained results demonstrates that there is a correlation between toughness, heat input and the MA constituent morphology, in a way that lower values of absorbed energy were obtained as the simulated heat input increased. In this condition, it was also observed that the MA constituent showed a greater tendency to become more globular than elongated.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-02-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.