Disertación de Maestría
DOI
Documento
Autor
Nombre completo
Daniel Uliana
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Director
Tribunal
Kahn, Henrique (Presidente)
Andrade, Fábio Ramos Dias de
Delboni Júnior, Homero
Título en portugués
Caracterização tecnológica do minério de fosfato do complexo alcalino de Salitre, MG - área Fosfertil.
Palabras clave en portugués
Análise de imagens
Apatita
Caracterização tecnológica
Minério de fosfato
Resumen en portugués
O presente estudo refere-se à caracterização tecnológica de tipos de minério de fosfato residual do complexo alcalino-carbonatítico de Salitre (MG), em área de interesse da Fosfertil. O procedimento experimental consistiu de moagem das amostras abaixo de 0,21 mm, análise granulométrica por peneiramento a úmido e separações minerais (líquido denso e Frantz). A composição mineralógica bem como a liberação da apatita e suas formas de associação com a ganga foram determinadas através de sistema de análise de imagens por feixe de elétrons (Mineral Liberation Analyser), com apoio de análises por DRX e MEV/EDS. As composições químicas dos produtos gerados foram determinadas por FRX. Seis amostras com graus distintos de intemperismo foram estudadas: apatitito (APAT), foscorito intemperizado (FIT), foscorito silicificado (FST), zona de mistura (ZMT), piroxenito intemperizado (PIT) e piroxenito (PXT). Os teores de P2O5 variam de 9 a 25% e a composição mineralógica é similar para todas as amostras, variando apenas as proporções relativas entre as espécies minerais. As amostras mais intemperizadas (APAT e FIT) são basicamente constituídas por apatita e magnetita; a amostra PIT apresenta também conteúdos elevados de filossilicatos e quartzo. Já as amostras menos intemperizadas (PXT, FST e ZMT) contêm maiores proporções de filossilicatos e diopsídio, principalmente a amostra PXT. A parcela de fósforo não apatítico varia de 10 a 20% nas amostras PIT e FIT e de 1 a 6% nas demais, sendo mais expressiva nos finos (<0,020 mm). Para cominuição abaixo de 0,21 mm, o conteúdo de finos varia de 20 a 34% e a parcela de fósforo associada a estes é de 13 e 16% nas amostras APAT, FIT e PIT e de 19 a 21% nas demais. Acima de 0,020 mm, a apatita representa de 96 a 98% do P2O5 (89% na amostra PIT); a liberação da apatita é superior a 90% nas amostras APAT, FIT e PIT, variando de 85 a 89% nas demais. Os resultados obtidos sugerem que a composição mineralógica e suas formas de associação não devem opor maiores dificuldades à concentração da apatita por flotação, podendo-se, em princípio, restringir a variabilidade do minério estudado a três tipos principais para fins de processamento mineral.
Título en inglés
Technological characterization of phosphate ore from Salitre alkaline-carbonatitic complex, MG - Fosfertil area.
Palabras clave en inglés
Apatite
Image analysis
Phosphate ore
Technological characterization
Resumen en inglés
The present study refers to the technological characterization of residual phosphate ore types from Salitre alkaline-carbonatitic complex (MG), in Fosfertil area. The procedure comprised grinding the samples bellow 0.21 mm, size analysis by wet screening and mineral separations (heavy liquid and Frantz). Mineralogical composition as well as apatite liberation and its associations to gangue minerals were determined by SEM-based image analysis (Mineral Liberation Analyser) and supported by XRD and SEM/EDS. Chemical compositions of all generated products were determined by XRF. Six samples with different weathering grades were studied: apatitite (APT), weathered foskorite (FIT), silicified foskorite (FST), mixture zone (ZMT), weathered piroxenite (PIT) and piroxenite (PXT). The P2O5 grades vary from 9 to 25% and mineralogical composition is similar to all samples, varying only the relative proportions among mineral species. The deeply weathered samples (APAT and FIT) are basically constituted by apatite and magnetite; PIT shows also high content of phyllosilicates and quartz. On the other hand, the less weathered samples (FST, ZMT and PXT) have major amounts of phyllosilicates and diopside, especially PXT. The non-apatitic phosphor varies from 10 to 20% in samples PIT and FIT and from 1 to 6% in the others; these contents are mostly expressive in fines (<0.020 mm). The fine content, considering comminution under 0.21 mm, varies between 20 and 34% w/w, while the related distribution of apatitic phosphor corresponds from 13 to 16% in the samples APAT, FIT and PIT and from 19 to 21% in the others. Above 0,020 mm, apatite represents 96 to 98% of total phosphor (89% in sample PIT); its liberation grade overcomes 90% in APAT, FIT and PIT, varying from 85 to 89% in the other samples. The results suggest that mineralogical composition and its associations should not oppose major difficulties to apatite concentration by froth flotation and that might be possible to restrict the ore variability to three main oretypes for mineral processing.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-12-23
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • ULIANA, Daniel, KAHN, Henrique, and BRAZ, André Borges. Caracterização tecnológica dos tipos de minério de fosfato do Complexo Alcalino de Salitre, MG - Área Fosfertil [doi:10.1590/S0370-44672009000400015]. Rem: Revista Escola de Minas [online], 2009, vol. 62, n. 4, p. 511-516.