Master's Dissertation
DOI
10.11606/D.3.2004.tde-11022005-162828
Document
Author
Full name
Maurício de Carvalho Silva
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2004
Supervisor
Committee
Ruggieri, Claudio (President)
Bose Filho, Waldek Wladimir
Magnabosco, Rodrigo
Title in Portuguese
Caracterização das propriedades mecânicas e metalúrgicas do aço API 5L X 80 e determinação experimental de curvas J-R para avaliação da tenacidade a fratura.
Keywords in Portuguese
aços ARBL
API 5L X80
curvas J-R
delaminações
fratura dúctil
mecânica da fratura
mecânica da fratura elasto-plástica
propriedades mecânicas
tenacidade dos materiais
Abstract in Portuguese
Caracterizar propriedades de resistência à propagação de trinca em materiais dúcteis é um elemento central em métodos de avaliação de integridade estrutural de dutos destinados ao transporte de gás, petróleo e seus derivados que utilizam os aços ARBL. Sendo assim, o objetivo deste trabalho foi estudar as propriedades de fratura dúctil do aço API 5L X80, através da obtenção da curva de resistência à propagação estável de defeitos (curvas J-R) do material. O ensaio de tenacidade à fratura para obtenção da curva J-R foi conduzido utilizando a técnica do corpo-de-prova único (single specimen) empregando o método da flexibilidade no descarregamento (unloading compliance), segundo a norma de ensaios ASTM E1820-96. Os corpos-de-prova compactos C(T) apresentaram espessura B=15mm, largura W=2B e uma relação aproximada entre o tamanho de trinca (a) e a largura, a/W=0,6. O ensaio foi conduzido numa máquina universal de ensaios (MTS) servo-controlada e capacidade máxima de 250kN. Adicionalmente, foram conduzidos ensaios convencionais de tração (limite de escoamento – 550MPa, limite de resistência – 676MPa e alongamento total em 50mm – 27%), ensaios de impacto Charpy (energia absorvida de 220J à 0ºC – sentido longitudinal) e análises metalográficas (microestrutura refinada composta por ferrita, colônias de perlita e presença do constituinte MA). Tais caracterizações permitirão uma maior precisão na comparação da curva J-R do aço API 5L X80 em estudo com estudos futuros de tenacidade à fratura.
Title in English
Experimental investigation of ductile crack growth in an API 5L X80 pipeline steel using J-R curves.
Keywords in English
API 5L X80
delaminations
ductile crack growth
elastic plastic fracture mechanics (EPFM)
HSLA steel
J-R curves
Abstract in English
Assessments of crack growth resistance in ductile materials play a key role in structural integrity procedures for high strength, low alloy (HSLA) pipeline steels commonly employed in gas and petroleum trasmission systems. This work presents an investigation of the ductile tearing properties for an API 5L X80 pipeline steel using experimentally measured crack growth resistance curves (J-R curves) for the material. Testing of the X80 pipeline steel employed compact tension (C(T)) fracture specimens to determine the J-R curves based upon the unloading compliance method using a single specimen technique in accordance with the ASTM E1820 standard procedure. The C(T) specimens have thickness B=15mm, width W=2B and a ratio between crack size (a) and width, a/W=0,6. The experimental tests utilized a 250 kN MTS universal machine. Conventional tensile tests were also performed to determine the tensile properties for the tested material: yield strength of 550MPa, tensile strength of 676MPa and elongation of 27% (gage length of 50 mm). The Charpy V-notch impact tests also provided and absorbed energy of 220J at 0ºC. The metallographic analysis showed colonies of perlite and MA constituent islands in a ferrite matrix. This experimental characterization provides additional toughness and mechanical data against which the general behavior of X80 class pipeline steel can be compared.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2005-02-25
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.