Master's Dissertation
DOI
10.11606/D.3.2016.tde-04012016-171021
Document
Author
Full name
Caroline Badin
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2015
Supervisor
Committee
Giudici, Reinaldo (President)
Sayer, Claudia
Valera, Ticiane Sanches
Title in Portuguese
Síntese e caracterização de polímero híbrido acrílico-alquídico produzido por polimerização em miniemulsão.
Keywords in Portuguese
Desenho de experimento
Dispersão polimérica
Híbrido acrílico-alquídico
Miniemulsão
Nucleação secundária
Núcleo-casca
Abstract in Portuguese
Polímeros híbridos são caracterizados por conter numa mesma partícula dois tipos diferentes de polímero, normalmente incompatíveis e ligados por ligações covalentes. Neste trabalho, a síntese de um polímero híbrido acrílico-alquídico pelo processo de miniemulsão foi investigada. Com o objetivo de compreender como diferentes variáveis na fórmula afetam as características físico-químicas finais do látex, um planejamento experimental foi desenhado com o auxílio do software DX9 e os resultados analisados por modelos empíricos de superfície de resposta. Os fatores variados (variáveis independentes) foram: quantidade de co-estabilizante, surfactante e iniciador. Cada um dos fatores contribuiu para a alteração de pelo menos uma característica avaliada, e a sinergia entre eles afeta diretamente o teor de RDG, resposta indicativa do grau de grafitização entre as espécies. O coestabilizante contribuiu para o aumento do diâmetro médio de gotas e da polidispersidade de tamanho de partículas, enquanto reduziu a dureza do filme. A concentração de surfactante alterou o número de partículas por litro, reduzindo o diâmetro médio de partículas e aumentando a polidispersidade. O iniciador aumentou a conversão monomérica. Todas as dispersões de polímero híbrido produzidas apresentaram redução do tamanho médio de gotas para partículas, indicando evidência de nucleação secundária. As avaliações por microscopia eletrônica de transmissão (TEM) e microscopia de força atômica (AFM) mostraram que a morfologia obtida é do tipo núcleo-casca.
Title in English
Synthesis and characterization of alkyd-acrylic hybrid polymer produced by miniemulsion polymerization.
Keywords in English
Alkyd-acrylic hybrid
Core-shell
Design of experiment
Miniemulsion
Polymer dispersion
Secondary nucleation
Abstract in English
Hybrid polymers are defined by the presence of two or more different kinds of polymers in the same particle, typically incompatible and linked by covalent bonds. In this work, the synthesis of an alkyd-acrylic hybrid polymer produced by miniemulsion polymerization has been investigated. With the goal of understanding how different variables in the recipe affect the final characteristics of the latex, a design of experiment was planned using DX9 software and the results were analyzed by response surface methodology. The factors studied (independent variables) were: amount of co-stabilizer, surfactant and initiator. Each of these factors contributed to change at least one of the evaluated characteristics, and the synergy between them directly affects the RDG content, response of the polymer degree of grafting. Costabilizer contributed to increase the average droplets diameter and polydispersity of particle size, while reducing the film hardness. The amount of surfactant changed the number of particles, reducing the average particle size and increasing polydispersity. Initiator increased the monomer conversion. All hybrids dispersions presented a decrease in the droplet size to particle size, indicating evidence of secondary nucleation. Core-shell morphology was observed through transmission electron microscopy (TEM) and atomic force microscopy (AFM).
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Catalogacao.pdf (4.95 Kbytes)
Dissert_Caroline.pdf (2.62 Mbytes)
Publishing Date
2016-01-12
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.