Disertación de Maestría
DOI
10.11606/D.3.2018.tde-04102018-091517
Documento
Autor
Nombre completo
Natalia Bahia Barbosa
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2018
Director
Tribunal
Giudici, Reinaldo (Presidente)
Hirota, Wilson Hideki
Lona, Liliane Maria Ferrareso
Título en portugués
Copolimerização de estireno e VeoVa 10: determinação das razões de reatividade e estudo do processo de polimerização em emulsão.
Palabras clave en portugués
Copolimerização
Estireno
Monitoramento
Polimerização
Processos químicos
Razão de reatividade
Resinas sintéticas
Veova-10
Resumen en portugués
Neste trabalho foram determinadas as razões de reatividade para a copolimerização entre estireno e VeoVa-10 através de estudo experimental de copolimerização em solução em tolueno. Os parâmetros foram obtidos através do ajuste aos dados experimentais dos modelos de Mayo-Lewis e Meyer-Lowry, utilizando o critério dos erros-nas-variáveis (método dos mínimos quadrados não-linear que considera a existência de erros em todas as variáveis medidas). A metodologia experimental desenvolvida, de polimerização em solução em ampolas preparadas dentro de uma glove box e submetidas a temperatura de 80°C, resultou em baixa conversão dos monômeros, adequada para a estimação das razões de reatividade pelos modelos. As amostras foram analisadas quantitativamente por espectroscopia de infravermelho para determinar, ao longo da reação, a conversão e as frações molares de cada um dos monômeros na mistura, sendo a composição do copolímero obtida pelo consumo dos monômeros. Foram obtidos valores de razões de reatividade bastante diferentes (restireno = 49.926 e rVeoVa10 = 1,062), evidenciando que a copolimerização destes monômeros em batelada leva a grandes desvios de composição, com tendência à formação de dois homopolímeros. O mesmo sistema de copolimerização foi também estudado no processo de polimerização em emulsão, em processos batelada alimentada e batelada intermitente. A conversão global dos monômeros e a distribuição de diâmetro médio das partículas foram analisadas durante a reação através das amostras coletadas ao longo do processo. Os efeitos das estratégias de alimentação avaliados foram apenas preliminares, pois não apresentaram resultados conclusivos.
Título en inglés
Copolymerization of styrene and VeoVa 10: determination of the reactivity ratios and study of the emulsion polymerization process.
Palabras clave en inglés
Copolymerization
Reactivity ratios
Styrene
Veova-10
Resumen en inglés
In this work the reactivity ratios for the copolymerization between styrene and VeoVa-10 were determined through an experimental study of solution copolymerization in toluen. The parameters were obtained by fitting the experimental data with the Mayo-Lewis and Meyer-Lowry models using the error-in-variables criterion (non-linear least squares method that considers the existence of errors in all measured variables). The experimental methodology developed, solution polymerization in ampoules prepared in a glove box and reacted at 80 °C, resulted in low conversion of the monomers, suitable for estimation of the reactivity ratios by the models employed. The samples were analyzed quantitatively by infrared spectroscopy to determine, during the reaction, the conversion and the mole fractions of each monomer in the mixture, the composition of the copolymer being obtained by the consumption of the monomers. Very different reactivity ratios were obtained (rstyrene = 49.926 and rVeoVa10 = 1.062), showing that the batch copolymerization of these monomers leads to large composition drift, with a tendency to form two homopolymers. The same copolymerization system was also tested in emulsion polymerization process, in semi-continuous and intermittent batch modes. The overall conversion of the monomers and the mean particle diameter distribution were analyzed during the reaction through the samples collected throughout the process. The effects of the feeding strategies evaluated were only preliminary, as they did not present conclusive results.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-10-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.