Tesis Doctoral
DOI
10.11606/T.3.2007.tde-08012008-150706
Documento
Autor
Nombre completo
Laura Gonçalves Carr
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2007
Director
Tribunal
Büchler, Pedro Maurício (Presidente)
Parra, Duclerc Fernandes
Ponce, Patrícia
Toffoli, Samuel Márcio
Valenzuela Díaz, Francisco Rolando
Título en portugués
Desenvolvimento de embalagem biodegradável tipo espuma a partir de fécula de mandioca.
Palabras clave en portugués
Amido
Embalagens
Polímeros (materiais)
Resumen en portugués
Este projeto tem por objetivo o desenvolvimento de uma embalagem biodegradável tipo espuma, obtida a partir de fécula de mandioca, para o armazenamento de alimentos. As espumas foram obtidas pelo processo de termo-expansão de uma massa de amido, água e aditivos. O estudo das formulações foi dividido em três etapas: na primeira etapa, foi estudada a influência dos sólidos na espuma, foram feitas 5 formulações variando a quantidade de sólidos. Na segunda etapa foi estudada a influência dos plastificantes na espuma e foram testados quatro diferentes plastificantes (PEG 300, PEG 1500, PEG 6000 e PVA). Na terceira etapa foi estudada a influência das cargas minerais nas espumas, foram adicionadas três diferentes tipos de cargas (caulim, talco, CaCO3) em diversas concentrações (0,1; 0,5; 1; 5; 10; 20 e 30%). Em todas as formulações foram analisadas a perda de produção e as características mecânicas das espumas. Os resultados indicaram que a quantidade de fécula influencia a viscosidade da massa, e a mesma está diretamente ligada à perda de produção das espumas. No estudo dos plastificantes, dentre os PEGs, o que apresentou melhor interação com o polímero foi o de menor massa molar (PEG 300), com espumas mais resistentes e flexíveis. As espumas produzidas com PVA apresentaram uma estrutura interna mais homogênea, com alvéolos menores e uniformes em relação às espumas com PEG 300. Isso ocorreu devido o PVA ter propriedades adesivas. A adição de cargas minerais diminuiu a flexibilidade e a resistência à compressão das espumas conforme a quantidade de carga adicionada. Isso indica que não houve uma boa adesão entre as cargas e o polímero (fécula). Verificou-se um acúmulo das cargas inorgânicas na superfície das espumas. As espumas sem adição de carga apresentaram boas características mecânicas, compatíveis com as embalagens comerciais. Foi feita a análise de biodegradabilidade por perda de massa e a espuma se degradou em 20 dias. Tanto a espuma, como os ingredientes utilizados para sua produção (plastificante, amido) não apresentaram toxicidade. Para encerrar o trabalho foi realizada uma análise para verificar a aceitação do produto pelos consumidores. Em todos os parâmetros avaliados (aparência, resistência, confiabilidade e intenção de compra) os consumidores aprovaram o produto.
Título en inglés
Development of biodegradable packaging, a starch foam, obtained by cassava starch.
Palabras clave en inglés
Biodegradable packaging
Food packaging
Mechanical properties
Starch
Resumen en inglés
The objective of this project is the development of biodegradable food packaging, starch foam, made by cassava starch. Starch foam was obtained with a batter of starch, water and additive, through thermo expansion process. Formulation study was divided in three parts: the first step was to verify the starch quantity influence in the starch foam and five formulations with different starch quantities were tested. The second step was to verify the plasticizer influence in the starch foam and four plasticizers were tested (PEG 300, PEG 1500, PEG 6000 and PVA). The third step was to verify the filler influence in the starch foam and three different filler kind were tested (kaolin, talc, CaCO3) in different quantities (0,1; 0,5; 1; 5; 10; 20 and 30%). Mechanical properties and lost of production of starch foam were analyzed in all formulations. Results of first step indicated that the starch quantity in the formulation influenced the batter viscosity and the lost of production of the starch foams. In the second step, the plasticizer PEG 300 (with low molecular weight) presented better performance as compared with PEG 1500 and PEG 6000. Starch foam with PVA presented internal structure more homogeneous than starch foam with PEG 300, due the PVA adhesiveness properties. In the third step, the filler addition did not improve the mechanical properties of starch foam, due there was not interaction between the filler and the polymer (starch). Observing the MEV, there were filler accumulated in the starch foam surface. According biodegradable analysis, starch foam degraded in 20 days. Even starch foam, as all the ingredients (starch, plasticizer), did not present toxicity. Starch foam without filler addition presented mechanical properties similar to the commercials food packaging made by expanded polystyrene and cardboard paper. To finish the work, was realized the acceptance analysis to verity the acceptability of the starch foam. As result, all parameters analyzed (appearance, resistance, trusty and purchase intention) were approved by consumers.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-04-03
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.