Master's Dissertation
DOI
10.11606/D.3.2006.tde-22072007-175250
Document
Author
Full name
Isabella Pacifico Aquino
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2006
Supervisor
Committee
Aoki, Idalina Vieira (President)
Benedetti, Assis Vicente
Guedes, Isabel Correia
Title in Portuguese
Caracterização da superfície do aço-carbono ABNT 1008 revestida com organo-silanos por meio de técnicas eletroquímicas e físico-químicas.
Keywords in Portuguese
Aço-carbono
Corrosão
Espectroscopia de impedância eletroquímica
Infravermelho
Silanos
Abstract in Portuguese
O objetivo deste trabalho foi caracterizar por meio de técnicas eletroquímicas e físicoquímicas o comportamento das camadas de silano aplicadas diretamente sobre as chapas de aço-carbono ABNT 1008 pela técnica de imersão, como uma proteção contra a corrosão. O estudo compreendeu a avaliação do comportamento das monocamadas de BTSE [Bis-1,2-(trietoxisilil)etano], VS (Viniltrietoxisilano) e BTSPA [Bis-(y-trimetoxisililpropil)amina], variando as condições de cura (tempo e temperatura) e também da dupla camada de silano. A dupla camada consistiu na combinação de BTSE como primeira camada e uma segunda camada de VS ou BTSPA. A espectroscopia de impedância eletroquímica (EIS) em solução de NaCl 0,1 M possibilitou detectarem a resistência à corrosão das camadas de silano, revelando que a sua eficiência aumenta com o aumento da temperatura e do tempo de cura e também que uma dupla camada apresenta um efeito protetor mais eficiente que o das monocamadas. Assim, a dupla camada de BTSE + BTSPA forneceu o melhor resultado, comprovando que confere melhor proteção ao aço-carbono. Com a medida ângulo de contato foi possível caracterizar a hidrofobicidade da superfície metálica revestida com o filme de silano, constatando-se que as camadas de BTSE, VS e BTSPA, e as duplas camadas curadas em altas temperaturas são mais hidrofóbicas que o aço-carbono. As curvas de polarização confirmaram os resultados obtidos por EIS, mostrando que a densidade de corrente de corrosão (icorr) diminui com o tempo e a temperatura de cura. A espectroscopia no infravermelho (IR) permitiu acompanhar a extensão da reação de polimerização dos silanos. A microscopia eletrônica de varredura (SEM) e as análises por espectroscopia de energia dispersiva de Raios-X (EDX) evidenciaram o efeito da cura na morfologia e topografia da superfície. Logo, conclui-se que os filmes à base de silanos como pré-tratamentos de aço são eficientes contra a corrosão.
Title in English
Characterization of the surface of steel-carbon ABNT 1008 coated with organo-silanes by means of electrochemical and physical-chemistry techniques.
Keywords in English
Corrosion
Electrochemical impedance spectroscopy
Infrared
Silanes
Steel-carbon
Abstract in English
The aim of this work is to characterize by means of electrochemical and physicochemical techniques the behavior of the silane layers applied directly on steel plates as a protection against corrosion. The silane film was obtained by the dip coat technique. This study present the evaluation of the behavior of monolayers of BTSE [Bis-1,2- (triethoxysilyl)ethane, BTSPA [Bis-(y-trimethoxysilylpropyl)amino] and VS (Vinyltriethoxysilane), varying the curing conditions (time and temperature) and also with a double silane layer, consisting of a combination of BTSE as first layer and a VS or BTSPA second layer. The electrochemical impedance spectroscopy (EIS) in a NaCl 0.1 M solution allowed the corrosion resistance assessment of the silane layers, showing that their protection efficiency increase for higher curing temperatures and curing times. Double layers were always more protective than monolayers. The contact angle measurements allowed to characterize the hydrophobicity of the metallic surface coated with the silane film, showing that the layers of BTSE, VS and BTSPA cured at higher temperatures are more hydrophobic and, therefore, more protective. The polarization curves confirmed the results obtained by EIS, showing that the corrosion current densities (icorr) decreased when the curing time and temperature were increased. The infrared spectroscopy (IR) showed the extension of the polymerization reaction of the silane layers. The SEM images and the EDX analyses evidenced the effect of the cure on the morphology and topography of the surface. Thus, the results lead to conclude that silane based films are good alternatives as pre-treatments for steel against corrosion.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
FichaCatalog.doc (31.50 Kbytes)
Publishing Date
2007-08-20
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.