Disertación de Maestría
DOI
10.11606/D.3.2006.tde-22072007-175250
Documento
Autor
Nombre completo
Isabella Pacifico Aquino
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2006
Director
Tribunal
Aoki, Idalina Vieira (Presidente)
Benedetti, Assis Vicente
Guedes, Isabel Correia
Título en portugués
Caracterização da superfície do aço-carbono ABNT 1008 revestida com organo-silanos por meio de técnicas eletroquímicas e físico-químicas.
Palabras clave en portugués
Aço-carbono
Corrosão
Espectroscopia de impedância eletroquímica
Infravermelho
Silanos
Resumen en portugués
O objetivo deste trabalho foi caracterizar por meio de técnicas eletroquímicas e físicoquímicas o comportamento das camadas de silano aplicadas diretamente sobre as chapas de aço-carbono ABNT 1008 pela técnica de imersão, como uma proteção contra a corrosão. O estudo compreendeu a avaliação do comportamento das monocamadas de BTSE [Bis-1,2-(trietoxisilil)etano], VS (Viniltrietoxisilano) e BTSPA [Bis-(y-trimetoxisililpropil)amina], variando as condições de cura (tempo e temperatura) e também da dupla camada de silano. A dupla camada consistiu na combinação de BTSE como primeira camada e uma segunda camada de VS ou BTSPA. A espectroscopia de impedância eletroquímica (EIS) em solução de NaCl 0,1 M possibilitou detectarem a resistência à corrosão das camadas de silano, revelando que a sua eficiência aumenta com o aumento da temperatura e do tempo de cura e também que uma dupla camada apresenta um efeito protetor mais eficiente que o das monocamadas. Assim, a dupla camada de BTSE + BTSPA forneceu o melhor resultado, comprovando que confere melhor proteção ao aço-carbono. Com a medida ângulo de contato foi possível caracterizar a hidrofobicidade da superfície metálica revestida com o filme de silano, constatando-se que as camadas de BTSE, VS e BTSPA, e as duplas camadas curadas em altas temperaturas são mais hidrofóbicas que o aço-carbono. As curvas de polarização confirmaram os resultados obtidos por EIS, mostrando que a densidade de corrente de corrosão (icorr) diminui com o tempo e a temperatura de cura. A espectroscopia no infravermelho (IR) permitiu acompanhar a extensão da reação de polimerização dos silanos. A microscopia eletrônica de varredura (SEM) e as análises por espectroscopia de energia dispersiva de Raios-X (EDX) evidenciaram o efeito da cura na morfologia e topografia da superfície. Logo, conclui-se que os filmes à base de silanos como pré-tratamentos de aço são eficientes contra a corrosão.
Título en inglés
Characterization of the surface of steel-carbon ABNT 1008 coated with organo-silanes by means of electrochemical and physical-chemistry techniques.
Palabras clave en inglés
Corrosion
Electrochemical impedance spectroscopy
Infrared
Silanes
Steel-carbon
Resumen en inglés
The aim of this work is to characterize by means of electrochemical and physicochemical techniques the behavior of the silane layers applied directly on steel plates as a protection against corrosion. The silane film was obtained by the dip coat technique. This study present the evaluation of the behavior of monolayers of BTSE [Bis-1,2- (triethoxysilyl)ethane, BTSPA [Bis-(y-trimethoxysilylpropyl)amino] and VS (Vinyltriethoxysilane), varying the curing conditions (time and temperature) and also with a double silane layer, consisting of a combination of BTSE as first layer and a VS or BTSPA second layer. The electrochemical impedance spectroscopy (EIS) in a NaCl 0.1 M solution allowed the corrosion resistance assessment of the silane layers, showing that their protection efficiency increase for higher curing temperatures and curing times. Double layers were always more protective than monolayers. The contact angle measurements allowed to characterize the hydrophobicity of the metallic surface coated with the silane film, showing that the layers of BTSE, VS and BTSPA cured at higher temperatures are more hydrophobic and, therefore, more protective. The polarization curves confirmed the results obtained by EIS, showing that the corrosion current densities (icorr) decreased when the curing time and temperature were increased. The infrared spectroscopy (IR) showed the extension of the polymerization reaction of the silane layers. The SEM images and the EDX analyses evidenced the effect of the cure on the morphology and topography of the surface. Thus, the results lead to conclude that silane based films are good alternatives as pre-treatments for steel against corrosion.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
FichaCatalog.doc (31.50 Kbytes)
Fecha de Publicación
2007-08-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.