Disertación de Maestría
DOI
10.11606/D.3.2018.tde-23052018-084841
Documento
Autor
Nombre completo
Kristine Bruce Wanderley
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2018
Director
Tribunal
Tenório, Jorge Alberto Soares (Presidente)
Barros, Alexandre Martins
Brocchi, Eduardo de Albuquerque
Título en portugués
Recuperação de magnésio do licor de lixiviação de minério limonítico por cristalização.
Palabras clave en portugués
Cristalização
Limonita
Lixiviação
Solubilidade
Resumen en portugués
No processo de obtenção de níquel de fontes de minério limonita, a lixiviação ácida do minério resulta na dissolução de íons metálicos em uma solução aquosa. Com o uso da tecnologia apropriada, é possível recuperar esses íons metálicos em vez de descartá-los. O presente estudo tem como objetivo a recuperação de magnésio de uma solução contendo íons magnésio e sulfato utilizando-se a técnica da cristalização a alta temperatura. A aplicação da cristalização a alta temperatura para recuperar o magnésio na forma de sulfato de magnésio hidratado pode ser vantajosa uma vez que sua decomposição térmica resulta em MgO e SO2, produtos que podem ser reutilizados no processo de mineração da limonita. Isso reduz o volume de resíduo formado e custo de reagentes no processo. Foi projetado um sistema de cristalizador acoplado a filtração e foi verificado a influência da temperatura, tempo de residência e pH da solução na quantidade de magnésio cristalizado. A solução residual de cada batelada foi analisada por cromatografia de íons para quantificar o magnésio na solução. Os cristais formados foram analisados utilizando-se a técnica de difração de raios-X (DRX), por microscopia eletrônica de varredura (MEV-EDS) e agitamento de peneiras a fim de avaliar a composição química, morfologia e granulometria dos cristais. A solubilidade do sulfato de magnésio foi determinada experimentalmente com o intuito de ampliar a compreensão da solubilidade do sal e obter valores de Kps. Em 5 horas de tempo de residência o sistema foi estabilizado, indicando que não haverá mais crescimento cristalino em tempos de residência maiores que 5 horas. Em pH 5,7 a 230°C e em 5 horas de tempo de residência ocorreu a maior remoção de magnésio com cerca de 81% cristalizado. Os cristais apresentaram morfologia esférica com exceção do cristal obtido a 230 °C em pH 2, que apresentou formato retangular. A análise por DRX mostrou a presença de um produto constituído majoritariamente por sulfato de magnésio monohidratado.
Título en inglés
Recovery of magnesium from limonite ore leach liquor by crystallization.
Palabras clave en inglés
High temperature crystallization
Limonite
Monohydrate
Solubility
Resumen en inglés
In the process of obtaining nickel from sources of limonite ore, the acid leaching of the ore results in the dissolution of metallic ions in solution. With the use of appropriate technology, it is possible to recover these metal ions instead of discarding them. The present study aims to recover magnesium from a solution containing magnesium and sulfate ions using high temperature crystallization. The application of high temperature crystallization to recover magnesium in the form of hydrated magnesium sulfate may be advantageous since its thermal decomposition results in MgO and SO2, products which can be reused in the limonite mining process. This reduces the volume of waste formed and the cost of reagents in the process. A crystallizer coupled to a filtration system was designed and the influence of the temperature, residence time and pH of the solution on the amount of crystallized magnesium from solution was investigated. The residual solution was analyzed by ion chromatography to quantify the magnesium in the solution. The crystals formed were analyzed by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM-EDS) and sieve shakers in order to evaluate the chemical composition, morphology and grain size of the crystals. The solubility of magnesium sulphate was determined experimentally to increase the understanding of the solubility of the salt and obtain values of Kps. In 5 hours of residence time the system was stabilized, indicating that there will be no more crystalline growth at residence times greater than 5 hours. At pH 5.7 at 230 ° C and in 5 hours of residence time 81% of Mg crystallized. The crystals presented spherical morphology except for crystals obtained at 230 °C, at pH 2, which presented a rectangular shape. XRD analysis showed the presence of a product consisting mainly of magnesium sulphate monohydrate.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-05-24
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.