Disertación de Maestría
DOI
Documento
Autor
Nombre completo
Marco Roberto Cavallari
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Director
Tribunal
Fonseca, Fernando Josepetti (Presidente)
Faria, Roberto Mendonça
Martino, João Antonio
Título en portugués
Desenvolvimento de uma metodologia de fabricação de transistores de filmes finos orgânicos.
Palabras clave en portugués
Células solares
Processos de fabricação
Semicondutores
Transistores
Resumen en portugués
Neste trabalho, é apresentada uma metodologia de fabricação de transistores de filmes finos orgânicos. Foram fabricadas células solares de heterojunção de poli(3- hexiltiofeno) (P3HT) e [6,6]-fenil-C61-butirato de metila (PCBM) por apresentarem máxima conversão de potência (PCE) de cerca 5 %. Partindo de rendimentos de 10-6 até atingir 1,7 %, são mostradas as dificuldades no processamento de filmes orgânicos e na caracterização destes dispositivos. Destacam-se dentre outros, a importância da geometria dos eletrodos, da preparação da solução de blendas orgânicas e dos cuidados na utilização de substratos flexíveis (e.g. polietileno tereftalato PET). A estrutura empregada é composta por vidro, óxido de índio dopado com estanho (ITO), poli(3,4- etilenodioxitiofeno) complexado com poli(ácido estireno-sulfônico) (PEDOT:PSS), P3HT:PCBM, fluoreto de lítio (LiF) e alumínio. PET coberto por In2O3/Au/Ag em substituição ao vidro-ITO é utilizado devido à busca da indústria eletrônica por materiais alternativos de baixo custo. Estrutura semelhante é empregada para caracterização da mobilidade dos portadores de carga em filmes orgânicos. Técnicas tais como Time of Flight (ToF), Charge Extraction in Linearly Increasing Voltage (CELIV), além da interpretação de curvas estacionárias de densidade de corrente por tensão (JxV) foram empregadas para estudo de derivados de poli(para-fenileno vinileno) (PPV). Foram obtidas mobilidades de 10-810-6 cm2/Vs para modelos de corrente limitada por carga espacial (SCLC) com armadilhas rasas e profundas. Mobilidades de efeito de campo caracterizadas em TFTs bottom gate bottom contact com porta comum são pelo menos duas ordens de grandeza superiores às obtidas através das técnicas anteriormente citadas. Foram utilizados diversos substratos (e.g. silício monocristalino e vidro-ITO), dielétricos (e.g. oxinitreto de silício (SiOxNy) por PECVD e SiO2 térmico), tratamentos de superfície (e.g. vapor de hexametildissilazana HMDS), semicondutores (derivados de PPV, P3HT, pentaceno) e eletrodos (e.g. camada de aderência de titânio). Definiu-se assim uma metodologia de seleção de novos semicondutores orgânicos para a indústria eletrônica.
Título en inglés
Development of a manufacturing methodology for organic thin film transistors.
Palabras clave en inglés
Manufacturing processes
Semiconductors
Solar cells
Transistors
Resumen en inglés
In this work, it is presented a methodology for organic thin-film transistor (OTFT) fabrication. Poly(3-hexylthyophene) (P3HT):[6,6]-phenyl-C61-butyric acidmethyl ester (PCBM) bulk heterojunction solar cells were studied for their maximum power conversion efficiency (PCE) around 5 %. Efficiencies evolution in time from 10-6 to 1.7 % show the difficulties involved in organic thin-film processing and device characterization. It is of remarkable importance the electrodes geometry, the organic blend solution preparation and the extra-care while processing on flexible substrates (e.g. polyethylene terephthalate PET). Devices are composed of indium tin oxide covered glass, poly(3,4-ethylenedioxythiophene) doped with poly(styrene sulfonic acid) (PEDOT:PSS), P3HT:PCBM active layer, lithium fluoride (LiF) and aluminum. PET covered with In2O3/Au/Ag substituting glass-ITO was employed due to the electronic industry research for low cost alternative materials. Similar structure is used for charge carrier mobility characterization. Techniques such as Time of Flight (ToF), Charge Extraction in Linearly Increasing Voltage (CELIV), and charge transport modeling of current density vs. voltage (JxV) stationary curves were applied on semiconductors like poly(para-phenylene vinylene) (PPV) derivatives. Mobilities around 10-810-6 cm2/Vs for space charge limited current (SCLC) with shallow and deep traps were obtained. Field effect mobilities characterized in bottom gate bottom contact TFTs with common gate are at least two orders higher than previous values. During this work, it was tested different substrates (e.g. monocrystalline silicon and glass-ITO), insulators (e.g. PECVD silicon oxynitride and thermal SiO2), surface treatments (e.g. hexamethyldisilazane vapor), semiconductors (PPV derivatives, P3HT, pentacene) and electrodes (e.g. titanium adhesion layer). It was defined that way a methodology of new semiconducting material selection for the electronic industry.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-11-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.