Disertación de Maestría
DOI
10.11606/D.3.2008.tde-06112008-105348
Documento
Autor
Nombre completo
Daniela de Assis Alvares
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Onmori, Roberto Koji (Presidente)
Drumond, Walker Soares
Possidonio, Shirley
Título en portugués
Estudo da influência da morfologia sobre as propriedades elétricas da blenda de PAni com EPDM desvulcanizado por microondas, proveniente do descarte da indústria de autopeças.
Palabras clave en portugués
Microeletrônica
Polímeros (materiais)
Tecnologia de microondas
Resumen en portugués
Blendas poliméricas de PAni dopada com ácido dodecilbenzeno sulfônico (PANI-DBSA) e copolímero etileno-propileno-monômero dieno desvulcanizado por microondas (dEPDM) foram obtidas por processo mecânico em diferentes concentrações. Caracterizações físico-químicas, morfológicas e elétrica foram realizadas para analisar as blendas. Um estudo sobre a desvulcanização da borracha EPDM foi descrito. Os ensaios de DSC mostraram temperaturas de transição vítrea diferentes nas blendas indicando que os componentes poliméricos não são totalmente miscíveis, o que permite a formação de uma rede condutora (PANI-DBSA) na matriz isolante (dEPDM). As análises de FTIR indicaram uma interação basicamente física entre o polímero PANI-DBSA e o copolímero dEPDM. As análises de raios-X confirmaram a presença de uma fase cristalina no interior das blendas atribuída à PANI-DBSA. Os ensaios de TGA mostraram que a PAni-DBSA diminuiu, significativamente, a estabilidade térmica do dEPDM. As análises de DMTA apresentaram a diminuição do amortecimento do sistema ocasionado pela presença da PAni, que é mais rígida, no segmento flexível do EPDM; ou seja, a mobilidade da cadeia fica mais limitada. Finalmente, o estudo de condutividade elétrica das blendas foi realizado e como esperado, esta aumenta com a concentração de PANIDBSA nas blendas, e um baixo limite de percolação pode ser observado devido à condutividade ocorrer para baixas concentrações de material condutor (<20%). A condutividade máxima alcançada foi de, aproximadamente, 102 S/cm para a composição de 50% de PANI-DBSA em massa.
Título en inglés
Study of morphology influence on the electric properties of the pani and devulcanizated EDPM blend.
Palabras clave en inglés
Blends
Conductive polymer
EPDM
Polyaniline
Rubber
Resumen en inglés
Polyaniline doped with dodecylbenzenesulfonic acid (PAni-DBSA) and ethylene-propylene-diene-monomer (EPDM) rubber devulcanizated by microwave (dEPDM) blends have been prepared by mechanical process. Flexible, free-standing and stretchable films have been obtained, which have been characterized by electrical conductivity measurements, FTIR, XRD, DSC, TGA, DMTA and SEM. Study about EPDM rubber devulcanization has been described. DSC analysis have showed different glass-transition temperatures in the blends and it has been observed that the compositions present enough compatibility to form a conductive network (PAni-DBSA) in the elastomeric matrix (dEPDM). By FTIR analysis, it has been noted that there was not modification about the spectrum of blends; therefore the interactions between the components were, basically, physics. X-ray analysis have confirmed the presence of a crystalline phase into the blends that is attributed by PAni-DBSA. TGA analysis have showed that the PAni-DBSA decreased significantly the rubber thermal stability. DMTA analysis have indicated that the system damping decreased according to the presence of PAni because of its stiffness. Finally, blends electric conductivity study has been carried out and as expected, the conductivity have increased with PAni-DBSA concentration in the blends and a low percolation threshold has been observed with the onset of conductivity occurring at lower concentrations of the conductive materials (<20%).
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-12-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.