Disertación de Maestría
DOI
10.11606/D.3.2003.tde-07052003-144030
Documento
Autor
Nombre completo
Katia Franklin Albertin
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2003
Director
Tribunal
Alvarez, Ines Pereyra de (Presidente)
Santos Filho, Sebastiao Gomes dos
Swart, Jacobus Willibrordus
Título en portugués
Estudo e fabricação de capacitores MOS com camada isolante de SiOxNy depositada por PECVD.
Palabras clave en portugués
capacitor MOS
densidade de estados de interface
oxinitreto de silício
PECVD
Resumen en portugués
Neste trabalho foram fabricados e caracterizados capacitores MOS com camada dielétrica de oxinitreto de silício de diferentes composição química, depositada pela técnica de PECVD a baixa temperatura, com o intuito de estudar suas propriedades dielétricas e de interface visando à aplicação deste material em dispositivos MOS e de filme fino. Os capacitores foram fabricados sobre lâminas de silício do tipo p que passaram pelo processo de limpeza química inicial, seguida da deposição da camada dielétrica, fotogravação, metalização e sinterização. Os filmes de SiOxNy, utilizados como camada dielétrica, foram depositados pela técnica de PECVD à temperatura de 320ºC variando os fluxos dos gases precursores de forma a obter filmes com diferentes composições químicas. Os capacitores MOS foram caracterizados por medidas de capacitância e corrente em função da tensão, de onde foram extraídas a densidade de estados de interface, a densidade de carga efetiva, constante dielétrica e campo elétrico de ruptura dos filmes. Os resultados mostraram uma variação linear da constante dielétrica do filme em função da concentração de nitrogênio, indo do valor de 3,9, correspondente ao dióxido de silício estequiométrico (SiO2) à 7,2 correspondente ao nitreto de silício estequiométrico (Si3N4). Também observamos que o nitrogênio é uma barreira eficiente à difusão de impurezas através do dielétrico. Porém, notamos uma grande dispersão de duas ordens de grandeza nos valores da carga efetiva (Nss) e de densidade de estados de interface (Dit). Por outro lado, controlando algumas variáveis de forma a manter constante o valor de Nss ( ~1012 cm-2), observamos uma variação de Dit em função da concentração de nitrogênio no filme, esta variação porém é pequena comparada com a dispersão de duas ordens de grandeza observada, que atribuímos assim a fatores externos. O menor valor obtido de Dit foi de 4,55.1010 eV-1.cm-2, que é ótimo para um filme obtido por PECVD, sem nenhum tratamento térmico e melhor que os reportados na literatura para dielétricos obtidos por técnicas que utilizam altas temperaturas (LPCVD-800ºC e oxinitretação térmica – 1100ºC). Assim, podemos concluir que a técnica de PECVD é promissora para a obtenção de dielétricos a baixas temperaturas.
Título en inglés
Study and fabrication of MOS capacitor with PECVD SiOxNy.
Palabras clave en inglés
interface state density
MOS Capacitor
silicon oxynitride
Resumen en inglés
In this work, MOS capacitors with different chemical composition silicon oxynitride insulating layer, deposited by PECVD technique at low temperature were fabricated and characterized, in order to study its dielectric and interface properties, seeking its aplication as insulating layer in MOS and thin films devices. The MOS capacitors were fabricated onto p-silicion wafers previously cleaned by a standard process, followed by the insulating layer deposition, photolitography, metalization and sinterization. The SiOxNy insulating layer was deposited by the PECVD technique at 320ºC changing the precursor gases flows to obtain films with different chemical compositions. The MOS capacitors were characterized by capacitance and current vs. voltage measurements, from where the interface state density (Dit), the effective charge density (Nss), the dielectric constant (k) and the film electrical breakdown field (Ebd) were extracted. The results showed a dielectric constant varying linearly as a function of the films nitrogen concentration, going from a value of 3.9, corresponding to stoichiometric silicon dioxide (SiO2) to a value of 7.2, corresponding to stoichiometric silicon nitride film (Si3N4). We also observed that nitrogen is an efficient diffusion barrier against contaminants. However, a large dispersion, about two orders of magnitude, in the effective charge and in the interface state density was observed. On the other hand, controlling some variables so as to keep the Nss value constant (~1012 cm-2) we observed a Dit variation as a function of the film nitrogen concentration, this variation is small when compared with the observed dispersion of two orders of magnitude, thus attributed to external factors. The smallest obtained Dit was 4.55.1010 eV-1.cm-2, which is unexpected for a PECVD film without any anealing process and is better than the values reported in the literature for dielectrics obtained at high temperatures techniques (as LPCVD – 800ºC and thermal oxynitridation – 1100ºC). Therefore, we can conclude that the PECVD technique is promising for obtaining low temperature dielectrics.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
katia.pdf (1.80 Mbytes)
Fecha de Publicación
2003-05-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.