Disertación de Maestría
DOI
10.11606/D.3.2013.tde-11072014-093623
Documento
Autor
Nombre completo
Shiva do Valle Camargo
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Tatumi, Sonia Hatsue (Presidente)
Mittani, Juan Carlos Ramírez
Santos Filho, Sebastião Gomes dos
Título en portugués
Confecção e caracterização de dosímetros luminescentes de cerâmicas de BaTiO3 nanoestruturadas.
Palabras clave en portugués
Dosimetria
Sol-Gel
Termoluminescência
Titanato de Bário
Resumen en portugués
Conforme pesquisas realizadas na literatura, o estudo do Titanato de Bário (BTO) na dosimetria é inédito, este material foi escolhido porque exibe propriedades luminescentes, demonstradas em experimentos de medidas de espectros de emissão. Para a confecção do BTO fez-se o uso da técnica química Sol-Gel, foi produzido amostras de BTO Puro, BTO dopado e co-dopado com diversas terras-raras. Todas as amostras produzidas sofreram calcinações com temperaturas definidas em 800, 1000 e 1200°C. As dopagens foram realizadas com os seguintes elementos terras-raras: Nd, Tb, Eu, Yb, Er, Pr, e as amostras co-dopadas foram com Tb/Eu e Yb/Er; no total foram confeccionadas trinta e uma amostras. No estudo de redução de massa foi constatada uma redução de metade das massas das amostras durante o processo de calcinação. Nas análises de Termoluminescência (TL) pelo menos uns dos tipos de calcinações apresentaram picos TL, com exceção das amostras co-dopadas com Tb/Eu. As amostras dopadas com Eu e Tb se destacaram nas análises das respostas termoluminescentes. A amostra com Tb e calcinada a 1200°C forneceu pico TL entre 90 a 200°C, e a dopada com Eu (1mol%) e calcinado a 1000°C apresentou picos TL em 110°C e 370°C. A mínima dose detectável para o pico de 110°C foi de 119 mGy e para o pico de 370°C foi de 143 mGy. As análises de MEV mostraram que as micrografias das amostras de BTO dopado tanto com Tb, quanto com Eu apresentaram superfícies porosas, diferentemente das Puras, que apresentaram superfície mais lisa. As análises de DRX indicaram uma fase tetragonal para as amostras Pura e dopadas com Eu (1 mol%), ambas calcinadas a 1000°C.
Título en inglés
Preparation and characterization of luminescent dosimeters nanostructured BaTiO3 ceramic.
Palabras clave en inglés
Barium Titanate
Dosimetry
Sol-Gel
Thermoluminescence
Resumen en inglés
According to the literature, the study of Barium Titanate (BTO) for dosimetry is unpublished yet, this material was chosen because it exhibits luminescent properties, demonstrated in emission spectra experiments. To make the BTO samples the chemical sol-gel technique was used. Samples of BTO Pure, doped and co-doped with different rare earths were made. All produced samples were calcinated with temperatures at 800, 1000 and 1200°C. The doping was performed with the following rare earths: Nd, Tb, Eu, Yb, Er, Pr, and some samples were co-doped with Tb / Eu and Yb / Er; in total were made thirty-one samples. In the study of weight reduction, a reduction, by half of the mass of raw material, was observed during the calcination process. In the TL analysis, at least one of the types (temperature) of calcinations provides TL peaks formation, except for the samples co-doped with Tb / Eu. The BTO: Eu and Tb provided the best TL response. The BTO: Tb and calcined at 1200°C showed TL peak at 90 to 200°C and the one doped with Eu (1mol%) and calcined at 1000°C supplied peaks at 110°C and 370°C. The minimum detectable dose to the TL peak at 110°C was 119 mGy and for TL peak at 370°C was 143 mGy. SEM analyzes showed that the micrographs of BTO samples doped with both Tb and Eu supplied porous surfaces, unlike the pure sample, that showed smoother surface. XRD analyzes indicated a tetragonal phase to pure sample and the one doped with Eu (1 mol%), both calcined at 1000°C.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-07-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.