Master's Dissertation
DOI
10.11606/D.3.2012.tde-18102012-103632
Document
Author
Full name
Leonardo Bontempo
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2012
Supervisor
Committee
Kassab, Luciana Reyes Pires (President)
Santos Filho, Sebastião Gomes dos
Wetter, Niklaus Ursus
Title in Portuguese
Caracterização elétrica de filmes finos de telureto com nanopartículas de ouro depositados pela técnica sputtering.
Keywords in Portuguese
Constante dielétrica
Filmes finos
high k
Nanopartícula metálica
Sputtering
Telureto
Abstract in Portuguese
Este trabalho tem como objetivo a produção e caracterização elétrica de filmes finos de telureto com nanopartículas de ouro para aplicações em microeletrônica. Filmes finos foram produzidos por magnetron sputtering a partir de alvos de telureto cerâmico e de ouro metálico. Foi desenvolvida metodologia adequada para a nucleação das nanopartículas de ouro por meio de tratamento térmico. Foram nucleadas nanopartículas de ouro a fim de que fossem observadas as influências nas propriedades elétricas. Os filmes foram depositados sobre substrato de silício e, para as medidas elétricas, ilhas de alumínio foram depositadas sobre o filme, utilizando-se os processos convencionais de microeletrônica: limpeza química, deposição por sputtering e evaporação. Com a finalidade de verificar a nucleação das nanopartículas metálicas, foram realizadas análises por Microscopia Eletrônica de Transmissão que indicaram a presença de nanopartículas metálicas, cristalinas, aproximadamente esféricas e com tamanho médio aproximado entre 1,5 e 5 nm. Outras técnicas de caracterização usadas foram microscopia de força atômica, perfilometria e extração de curvas da capacitância e condutância em função da tensão. Foram produzidos filmes com diversas espessuras com e sem nanopartículas de ouro. Por meio das medidas de capacitância em função da tensão foi possível determinar a influência das nanopartículas metálicas na constante dielétrica (k). Os resultados obtidos mostram aumento do valor de k de aproximadamente 70%, na presença de nanopartículas de ouro. Cabe ressaltar o resultado obtido para os filmes com espessura de 32,8 nm, para os quais o valor da constante dielétrica varia de 9,4 para 12,2, para tratamentos de 10 e 20 h, respectivamente. O material estudado tem possíveis aplicações em microeletrônica como dielétrico em capacitores e transistores MOS, e como camada de passivação em dispositivos de potência.
Title in English
Electrical characterization of tellurite thin films containing gold nanoparticles deposited by sputtering technique.
Keywords in English
Dielectric constant
high k
Metallic nanoparticles
Sputtering
Tellurite
Thin films
Abstract in English
This work has the objective of production and electrical characterization f tellurite thin films containing gold nanoparticles for microelectronic applications. Thin films have been produced by magnetron sputtering from ceramic tellurite and metallic gold targets. It was developed an appropriate methodology for the gold nanoparticles nucleation by means of heat treatment. Gold nanoparticles were nucleated in order to be observed the influence on the electrical properties. The films were deposited on silicon substrate and, to the electrical measurements, aluminium islands were deposited on the film, using the conventional processes of microelectronics: chemical cleaning, deposition by sputtering and evaporation. With purpose to check the metallic nanoparticles nucleation, transmission electron microscopy measurements were performed and indicated the presence of crystalline metallic nanoparticles, with spherical shape and with average size between 1.5 and 5 nm. Other characterization techniques were used as atomic force microscopy, profilometry and electrical measurements to obtain the capacitance and conductance curves. Films have been produced with different thicknesses with and without gold nanoparticles. From capacitance measurement, it was possible to determine the metallic nanoparticles influence on the dielectric constant (k). The results obtained showed the increase of k of about 70% with the presence of gold nanoparticles. We have to remark the results obtained for thin films with 32.8 nm thickness with k varying from 9.4 to 12.2, for heat treatments during 10 and 20 h, respectively. The material studied has possible applications in microelectronics as high-k dielectrics for capacitors and transistors MOS, and as passivation layer for power devices.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2012-10-26
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.