Disertación de Maestría
DOI
10.11606/D.3.2012.tde-18102012-103632
Documento
Autor
Nombre completo
Leonardo Bontempo
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2012
Director
Tribunal
Kassab, Luciana Reyes Pires (Presidente)
Santos Filho, Sebastião Gomes dos
Wetter, Niklaus Ursus
Título en portugués
Caracterização elétrica de filmes finos de telureto com nanopartículas de ouro depositados pela técnica sputtering.
Palabras clave en portugués
Constante dielétrica
Filmes finos
high k
Nanopartícula metálica
Sputtering
Telureto
Resumen en portugués
Este trabalho tem como objetivo a produção e caracterização elétrica de filmes finos de telureto com nanopartículas de ouro para aplicações em microeletrônica. Filmes finos foram produzidos por magnetron sputtering a partir de alvos de telureto cerâmico e de ouro metálico. Foi desenvolvida metodologia adequada para a nucleação das nanopartículas de ouro por meio de tratamento térmico. Foram nucleadas nanopartículas de ouro a fim de que fossem observadas as influências nas propriedades elétricas. Os filmes foram depositados sobre substrato de silício e, para as medidas elétricas, ilhas de alumínio foram depositadas sobre o filme, utilizando-se os processos convencionais de microeletrônica: limpeza química, deposição por sputtering e evaporação. Com a finalidade de verificar a nucleação das nanopartículas metálicas, foram realizadas análises por Microscopia Eletrônica de Transmissão que indicaram a presença de nanopartículas metálicas, cristalinas, aproximadamente esféricas e com tamanho médio aproximado entre 1,5 e 5 nm. Outras técnicas de caracterização usadas foram microscopia de força atômica, perfilometria e extração de curvas da capacitância e condutância em função da tensão. Foram produzidos filmes com diversas espessuras com e sem nanopartículas de ouro. Por meio das medidas de capacitância em função da tensão foi possível determinar a influência das nanopartículas metálicas na constante dielétrica (k). Os resultados obtidos mostram aumento do valor de k de aproximadamente 70%, na presença de nanopartículas de ouro. Cabe ressaltar o resultado obtido para os filmes com espessura de 32,8 nm, para os quais o valor da constante dielétrica varia de 9,4 para 12,2, para tratamentos de 10 e 20 h, respectivamente. O material estudado tem possíveis aplicações em microeletrônica como dielétrico em capacitores e transistores MOS, e como camada de passivação em dispositivos de potência.
Título en inglés
Electrical characterization of tellurite thin films containing gold nanoparticles deposited by sputtering technique.
Palabras clave en inglés
Dielectric constant
high k
Metallic nanoparticles
Sputtering
Tellurite
Thin films
Resumen en inglés
This work has the objective of production and electrical characterization f tellurite thin films containing gold nanoparticles for microelectronic applications. Thin films have been produced by magnetron sputtering from ceramic tellurite and metallic gold targets. It was developed an appropriate methodology for the gold nanoparticles nucleation by means of heat treatment. Gold nanoparticles were nucleated in order to be observed the influence on the electrical properties. The films were deposited on silicon substrate and, to the electrical measurements, aluminium islands were deposited on the film, using the conventional processes of microelectronics: chemical cleaning, deposition by sputtering and evaporation. With purpose to check the metallic nanoparticles nucleation, transmission electron microscopy measurements were performed and indicated the presence of crystalline metallic nanoparticles, with spherical shape and with average size between 1.5 and 5 nm. Other characterization techniques were used as atomic force microscopy, profilometry and electrical measurements to obtain the capacitance and conductance curves. Films have been produced with different thicknesses with and without gold nanoparticles. From capacitance measurement, it was possible to determine the metallic nanoparticles influence on the dielectric constant (k). The results obtained showed the increase of k of about 70% with the presence of gold nanoparticles. We have to remark the results obtained for thin films with 32.8 nm thickness with k varying from 9.4 to 12.2, for heat treatments during 10 and 20 h, respectively. The material studied has possible applications in microelectronics as high-k dielectrics for capacitors and transistors MOS, and as passivation layer for power devices.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2012-10-26
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.