Disertación de Maestría
DOI
10.11606/D.3.2006.tde-19092006-142354
Documento
Autor
Nombre completo
Michele Rodrigues
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2006
Director
Tribunal
Martino, Joao Antonio (Presidente)
Diniz, José Alexandre
Santos Filho, Sebastiao Gomes dos
Título en portugués
Caracterização elétrica de capacitores obtidos através de tecnologia ultra-submicrométrica.
Palabras clave en portugués
Capacitor
Corrente de tunelamento
Curva C-V
Efeito de depleção do Si-poli
MOS
Óxido de porta fino
Simulação bidimensional
Resumen en portugués
Apresentamos neste trabalho um estudo do efeito da depleção do silício policristalino e da corrente de tunelamento em dispositivos com óxidos de porta finos. Utilizamos curvas características da capacitância em função da tensão de porta (C-V), para analisar a degradação causada por estes efeitos.Quanto ao efeito da depleção do silício policristalino a capacitância total na região de inversão apresenta uma redução conforme a concentração de dopantes do silício policristalino diminui. Este efeito foi observado em curvas C-V tanto de alta como de baixa freqüência, sendo esta última mais afetada. A corrente de tunelamento através do óxido de porta apresentou uma influência na largura da região de depleção no silício, que aumentou devido ao tunelamento de portadores do substrato. Como resultado, uma diminuição na capacitância do silício foi observada, fazendo a curva C-V diminuir na região de inversão. Quando considerado o efeito de depleção no silício policristalino junto com o efeito do tunelamento, observou-se que na região da porta houve um excesso de portadores, causando uma diminuição na região de depleção do silício policristalino. Neste caso a curva C-V sofreu uma maior redução, tornando-se difícil separar os dois efeitos. A curva C-V de baixa freqüência foi a mais atingida, pois como os portadores tem tempo de resposta, pode-se observar a influência da corrente de tunelamento nas cargas de inversão. Apresentamos ainda um novo método para a determinação da concentração de dopantes no substrato e no silício policristalino, através de curvas C-V de alta freqüência. Simulações numéricas bidimensionais e medidas experimentais foram utilizadas para validação do método. Os resultados obtidos indicam que o método proposto apresenta um grande potencial, tendo como principal vantagem a simplicidade de aplicação.
Título en inglés
Electrical characterization of capacitors obtained through extreme-submicrometer technology.
Palabras clave en inglés
C-V curve
MOS capacitor
Polysilicon depletion effect
Thin gate oxide
Tunneling current
Two-dimensional simulation
Resumen en inglés
In this work we present the study of polysilicon depletion and the gate tunneling current effects in thin-gate oxide devices. Characteristic curves of capacitance as a function of the gate voltage (C-V) were used to analyze the degradation caused for these effects. Regarding the poly depletion effect, a reduction of the total capacitance in the inversion region was verified as the polysilicon doping concentration decreases. This effect was observed in C-V curves in high and low frequency, being the last one more affected. The gate tunneling current presented an influence on the width of the depletion silicon region, which increased due to the carriers tunneling from the substrate. As a result, a reduction in the silicon capacitance was observed, causing the C-V curve reduction in the inversion region. When the polysilicon depletion effect is considered together with the tunneling effect, it was observed that there is a carriers excess in the gate region, causing a reduction of the polysilicon depletion region width. In this case, the C-V curve suffered a larger reduction, making difficult to separate both effects. The most affected characteristic was the C-V curve at low frequency, due to existence of the carrier response time that allows observing the influence of the tunneling current in inversion charges. A new method for the determination of the doping concentration of substrate and polysilicon was also presented, through C-V curves at high frequency. Two-dimensional simulations and experimental measurements were used to validate the method. The obtained results indicate that the propose method present a higher potential, having as principal advantage the simplicity of application.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2006-11-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.