Tesis Doctoral
DOI
10.11606/T.3.2016.tde-21072016-105344
Documento
Autor
Nombre completo
Thiago Alexandre Alves de Assumpção
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2015
Director
Tribunal
Kassab, Luciana Reyes Pires (Presidente)
Barbosa, Eduardo Acedo
Ribeiro, Sidney José Lima
Santos Filho, Sebastião Gomes dos
Silva, Maria Lucia Pereira da
Título en portugués
Produção e caracterização de filmes finos amorfos de germanato codopados com Tm3+ e Yb3+ contendo nanopartículas metálicas para a produção de guias de onda.
Palabras clave en portugués
Filmes finos
Fotônica
Guias de onda
Itérbio
Nanopartículas metálicas
Túlio
Resumen en portugués
O trabalho em questão mostra a possibilidade de produção de guias de onda por meio de filme finos de GeO2-PbO codopados com Tm3+/Yb3+, com e sem nanopartículas (NPs) de ouro, a partir da técnica de RF Magnetron Sputtering. Foram usados nos processos de fabricação dos guias de onda do tipo RIB e PEDESTAL, as mesmas técnicas empregadas na fabricação de dispositivos de microeletrônica, tais como, litografia e corrosão por plasma. A influência dos parâmetros dos processos de produção é reportada e a caracterização dos guias foi realizada por diversas técnicas. Dentre elas, destacamos a microscopia eletrônica de varredura (MEV) para a observação do perfil dos guias, as rugosidades de superfície e as espessuras das camadas utilizadas para a confecção dos mesmos. Medidas de transmitância óptica realizadas nos filmes permitiram a determinação do coeficiente de absorção óptica e do índice de refração, de aproximadamente 2,0, além da confirmação das espessuras dos filmes obtidos por Sputtering. Guias do tipo RIB foram descartados por dificuldades enfrentadas durante o processo de fabricação. Medidas ópticas de perdas por propagação, realizadas em guias do tipo PEDESTAL, mostraram que os melhores guias produzidos apresentaram perdas em torno de 5 dB/cm em 633 e 1050 nm, e medidas de perfil de campo próximo, além da simulação dos modos propagados, o comportamento de guiamento multímodo. Ganho óptico em torno de 13,5 dB/cm (em 805 nm) foi obtido em guia com largura de 30 ?m e potência de bombeio estimada de ~75 mW. Guias contendo NPs de ouro foram produzidos por meio de metodologia adequada que permitiu a nucleação das NPs (tamanho médio de 20 nm) e um ganho 22 dB/cm em 805 nm, portanto, duas vezes superior ao mesmo guia sem NPs (30 ?m de largura). Os resultados apresentados demonstram que guias de onda GeO2-PbO codopados com Tm3+/Yb3+, com ou sem NPs metálicas, são promissores para aplicações em dispositivos fotônicos, com a criação de dispositivos amplificadores integrados para operação na 1° janela de telecomunicações.
Título en inglés
Production and characterization of Tm3+ and YB3+ codoped germanate amorphous thin films containing metallic nanoparticles for the production of waveguides.
Palabras clave en inglés
Metallic nanoparticles
Photonics
Thin films
Thulium
Waveguides
Ytterbium
Resumen en inglés
The work in question shows the possibility of producing waveguides by means of Tm3+/Yb3+ codoped GeO2-PbO thin films, with or without gold nanoparticles (NPs), by using the RF Magnetron Sputtering technique. For the production of RIB and PEDESTAL type waveguides, the techniques employed in the manufacture of microelectronics devices, such as plasma etching and lithography, were employed. The influences of the production process parameters are reported and the waveguides characterization was performed by several techniques. Among them, we highlight the scanning electron microscopy (SEM), which was used to observe the profile of the waveguides, the surface roughness and thickness of the layers used for their production. Measurements of thin films optical transmittance allowed the determination of the optical absorption coefficient and refractive index of approximately 2.0, and also the confirmation of the thin films thicknesses obtained by Sputtering. RIB type waveguides were discarded due to the difficulties during the manufacturing process. Optical measurements of propagation losses, held in the PEDESTAL type guides, showed losses around 5 dB/cm at 633 and 1050 nm, for the best waveguides produced, and near-field profile measurements in addition to the simulation of the propagating modes, showed multimode coupling behavior. Optical internal gain around 13.5 dB/cm (at 805 nm) was obtained in waveguide with 30 µm width at ~75 mW estimated power pumping. Waveguide containing gold NPs were produced using adequate methodology that allowed the NPs nucleation (average size of 20 nm) and 22 dB/cm gain at 805 nm, therefore, twice higher than the value obtained for the same waveguide without NPs (30 ?m width). These results show that Tm3+/Yb3+ codoped GeO2-PbO waveguides, with or without metallic NPs, are promising for applications in photonic devices, with the creation of integrated amplifiers devices for operation in the first telecommunications window.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-07-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.