Tesis Doctoral
DOI
10.11606/T.3.2016.tde-22092016-143235
Documento
Autor
Nombre completo
Francisco Araújo Bomfim Júnior
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2016
Director
Tribunal
Kassab, Luciana Reyes Pires (Presidente)
Santos Filho, Sebastião Gomes dos
Sene, Frank Ferrer
Silva, Maria Lucia Pereira da
Wetter, Niklaus Ursus
Título en portugués
Produção e caracterização de guias de ondas de germanato codopados com Er3+ e Yb3+ contendo nanopartículas metálicas para aplicações ópticas no infravermelho.
Palabras clave en portugués
Érbio
Filmes finos
Fotônica
Guias de onda
Nanopartículas metálicas
Resumen en portugués
O presente trabalho apresenta a produção e a investigação das propriedades ópticas de guias de onda vítreos baseados no sistema PbO-GeO2, codopados com íons de érbio de itérbio e contendo nanopartículas metálicas de ouro e prata, para aplicações como dispositivos fotônicos na terceira janela de telecomunicações (1530 nm). Os guias de onda foram obtidos por meio de processos convencionais utilizados em microeletrônica usando a técnica RF Magnetron Sputtering para deposição do material sobre uma estrutura do tipo PEDESTAL. Os primeiros guias produzidos apresentaram irregularidades laterais próximas ao núcleo que contribuíram para o aumento das perdas. Mudanças no processo de fabricação como a diminuição da espessura da máscara de cromo usada para a corrosão do SiO2, etapa adicional para a corrosão e a diminuição da espessura do guia de onda proporcionaram redução das perdas por propagação e aumento do ganho óptico em ~50% estimado em 6,0 dB/cm, em 1530 nm, para um guia de onda de 80 µm de largura. Entretanto, as dificuldades para medir guias com menores larguras levaram-nos a produzir guia de onda PEDESTAL utilizando SiO2 como máscara de corrosão do silício que permitiram redução significativa das irregularidades lateral; neste caso foi possível medir a perda e o ganho em guias com largura de até 1 µm. Acrescenta-se que guias de 6 µm tiveram aumento do ganho em 50% na presença de nanopartículas de ouro, atingindo 7,5 dB/cm para potência de bombeamento de 60 mW, portanto inferior à utilizada para o caso do guia sem nanopartículas de ouro, cuja saturação do ganho ocorreu em 100 mW. Guias com nanopartículas de prata foram também produzidos, obtendo-se ganho máximo de 4,0 dB/cm para um guia de 80 µm. Os resultados obtidos nos guias de onda PbO-GeO2 codopados com Er3+ e Yb3+ são promissores e mostram possibilidade de aplicação dos guias de onda como amplificadores ópticos na terceira janela de telecomunicações.
Título en inglés
Production and characterization of Er3+ and Yb3+ codoped germate waveguide with metallic nanoparticles for infrared optical applications.
Palabras clave en inglés
Erbium
Metallic nanoparticles
Photonics
Thin films
Waveguides
Resumen en inglés
This work presents the production and investigation of optical properties of erbium and ytterbium ions codoped PbO-GeO2 waveguides, containing metallic nanoparticles (NPs), for applications as photonic devices in the third window Telecommunications (1530 nm). The waveguides were obtained by microelectronics conventional processes and by RF Magnetron Sputtering technique using a pedestal type structure. The first pedestal waveguides presented irregulaties, in the lateral region, that contributed to the propagations losses enhancement. Changes in the fabrication process, as the decrease of the chromium used for SiO2 corrosion, additional step for the etching and decrease of the waveguide thickness provided reduction of the propagation losses and enhancement of the optical gain of about 50%; so we obtained 6.0 dB/ cm, at 1530 nm, for 80 µm waveguide width. The difficulty to measure waveguides with smaller width lead us to develop PEDESTAL waveguides using SiO2 as silicon mask for corrosion enabled the decrease of the roughness nearby the core. In this case it was possible to measure propagation losses and gain for waveguides width of 1 µm. It was obtained enhancement of 50 % for the waveguides with 6 µm width in the presence of gold NPs and the result was 7.5 dB/cm at 60 mW pumping power; for the case of the waveguide without gold NPs gain saturation occurred at 100 mW. Waveguides with silver NPs were also produced and the maximum gain was of 4.0 dB/cm for 80 µm. These results show the possibility of using Er3+and Yb3+ codoped PbO-GeO2 pedestal type waveguides as optical amplifiers in the third telecommunications window.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-10-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.