Disertación de Maestría
DOI
10.11606/D.3.2008.tde-25092008-140736
Documento
Autor
Nombre completo
Fernando Trevisan Saez Parra
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Santos Filho, Sebastião Gomes dos (Presidente)
Lucchi, Júlio César
Onmori, Roberto Koji
Título en portugués
Fabricação e caracterização de termopares Cu/CuNixPy obtidos por deposição eletroquímica.
Palabras clave en portugués
Eletrodeposição
Filmes finos
Sensor
Resumen en portugués
Neste trabalho foram estudadas deposições químicas de ligas CuNixPy e foram fabricados termopares Cu/CuNixPy sobre superfícies de lâminas de silício. Inicialmente, as superfícies foram pré-ativadas em uma solução diluída de ácido fluorídrico contendo PdCl2. Em seguida, foi empregado um banho químico alcalino diluído em água deionizada contendo 15 g/l NiSO4.6H2O; 0,1 a 0,3 g/l CuSO4.5H2O; 15 g/l Na2HPO2.H2O e 60 g/l Na3C6H5O7.2H2O na temperatura de 80OC sendo que NH4OH foi adicionado até que o pH do banho atingisse o valor de 8,0. Verificamos que a concentração do sal de cobre na solução de deposição afeta substancialmente a quantidade de cobre nos depósitos de CuNixPy. As concentrações planares e as composições dos filmes depositados foram obtidas através da técnica de espectrometria de retroespalhamento de Rutherford (RBS) e a morfologia superficial foi caracterizada através da técnica de microscopia de força atômica (AFM). A solução: 15 g/l NiSO4.6H2O + 0,3 g/l CuSO4.5H2O + 15 g/l Na2HPO2.H2O + 60 g/l Na3C6H5O7.2H2O + NH4OH (pH 8.0) na temperatura de 80OC foi a escolhida na obtenção da liga CuNiP0,5 para a construção de termopares Cu/CuNiP0,5 os quais apresentaram potência termoelétrica de aproximadamente (866) V/oC semelhante aos valores típicos apresentados na literatura para Cu/CuNi.
Título en inglés
Fabrication and characterization of Cu/CuNixPy thermocouples obtained by electroless deposition.
Palabras clave en inglés
Electroless deposition
Thermocouple
Thermoelectric power
Resumen en inglés
In this work, it was studied chemical depositions of CuNixPy alloys and it was fabricated Cu/CuNixPy thermocouples onto silicon wafer surfaces. Initially, surfaces were pre-activated in a diluted hydrofluoric acid solution containing PdCl2. Following, it was used a de-ionizedwater- diluted alkaline chemical bath containing 15 g/l NiSO4.6H2O; 0,1-0,3 g/l CuSO4.5H2O; 15 g/l Na2HPO2.H2O and 60 g/l Na3C6H5O7.2H2O at temperature of 80OC where NH4OH was added until ph was 8.0. The concentration of copper salt in the deposition solution greatly affected the Cu content of the CuNixPy deposits. Areal concentration and composition were measured by Rutherford Backscattering Spectrometry (RBS) and surface morphology was characterized by Atomic Force Microscopy (AFM). The solution: 15 g/l NiSO4.6H2O; 0.3 g/l CuSO4.5H2O; 15 g/l Na2HPO2.H2O; 60 g/l Na3C6H5O7.2H2O; NH4OH (pH 8.0) at the temperature of 80OC was chosen to obtain the CuNiP0.5 alloy to fabricate Cu/CuNiP0.5 thermocouples with thermoelectric power of about (866) V/oC, which is similar to the typical values reported in literature for Cu/CuNi.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
CapaseIndices.pdf (68.83 Kbytes)
Dissertacao.pdf (2.12 Mbytes)
Fecha de Publicación
2008-10-07
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.