Disertación de Maestría
DOI
10.11606/D.3.2006.tde-07122006-173150
Documento
Autor
Nombre completo
Rui Barbosa de Souza
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2006
Director
Tribunal
John, Vanderley Moacyr (Presidente)
Cincotto, Maria Alba
Kihara, Yushiro
Título en portugués
Suscetibilidade de pastas de cimento ao ataque por sulfatos - método de ensaio acelerado.
Palabras clave en portugués
Ataque por sulfatos
DRX
Durabilidade
Método de ensaio
Microestrutura
Sulfato combinado
TG
Resumen en portugués
O presente trabalho tem por objetivo investigar e propor uma metodologia rápida e eficaz de avaliação da reatividade do cimento Portland frente ao ataque por sulfatos. O método consiste na utilização de amostras de pasta de cimento hidratada em pó, colocadas em contato direto com soluções concentradas de Na2SO4 e MgSO4, em temperatura elevada (65ºC), para acelerar o ataque. Apesar dos cimentos estudados possuírem composição química parecida, os resultados de SO3 combinado mostraram que o cimento Classe G foi pouco menos suscetível ao ataque por sulfatos em função do maior teor de Fe2O3 presente. Da TG e DRX observou-se a formação de etringita no ataque por ambos os sais de sulfato; e formação de gipsita no ataque por MgSO4. Enquanto havia disponibilidade de portlandita na pasta hidratada, o cimento com adição mineral incorporada apresentou mesma taxa de ataque que os demais (sem adição), entretanto a partir do momento que toda a portlandita foi consumida, iniciou-se um processo de descalcificação do C-S-H, observado pela DRX.
Título en inglés
Susceptibility of cement pastes to sulfate attack - accelerated test method.
Palabras clave en inglés
Combined sulfate
Durability
Microstructure
Sulfate attack
TG
XRD
Resumen en inglés
The main point of this research is to propose a fast and effective method of evaluation of the cement reactivity to sulfate attack. Resistance to sulfate attack was measured by determining the combined sulfate in cement paste samples with exposure to Na2SO4 and MgSO4 solution, at high temperature (65°C). The samples of cement paste was triturated (powdered) in the proposed method. The results of combined SO3 showed that the Class G cement was little less susceptible to the sulfate attack because it has larger amount of Fe2O3. The ettringite formation was observed in the attack for both sulfate salts; and gypsum formation in the attack for MgSO4 (results of TG and XRD). The blended cement presented same results that the others, however when the Ca(OH)2 was totally consumed, it observed the decalcification of the C-S-H, by XRD.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
DissRUIBARBOSA.pdf (3.28 Mbytes)
DissRUIBARBOSAanexoA.pdf (928.57 Kbytes)
DissRUIBARBOSAanexoB.pdf (762.09 Kbytes)
FICHACATALOGRAFICA.doc (25.50 Kbytes)
Fecha de Publicación
2007-08-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.