Disertación de Maestría
DOI
10.11606/D.3.2007.tde-10012008-100734
Documento
Autor
Nombre completo
Flávio André da Cunha Munhoz
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2007
Director
Tribunal
Cincotto, Maria Alba (Presidente)
Kihara, Yushiro
Kuperman, Selmo Chapira
Título en portugués
Efeito de adições ativas na mitigação das reações álcali-sílica e álcali-silicato.
Palabras clave en portugués
Estruturas de concreto
Reação álcali-agregado (prevenção)
Resumen en portugués
A reação álcali-agregado é uma manifestação patológica diretamente ligada à seleção dos materiais (cimento, agregados miúdo e graúdo, água e aditivos) que pode comprometer a durabilidade das estruturas de concreto, uma vez que a interação desses materiais e as condições ambientais é que vão conferir ao concreto determinadas propriedades ligadas à sua vida útil. A reação entre os hidróxidos alcalinos solubilizados na fase líquida dos poros dos concretos e alguns agregados reativos é lenta e resulta em um gel que, ao se acumular em vazios do concreto e na interface pasta-agregado, na presença de água, se expande, exercendo pressão interna no concreto. Ao exceder a resistência à tração do concreto, a pressão interna pode promover fissurações. A reação álcali-agregado requer a atuação conjunta de água, agregado reativo e álcalis. Sua prevenção pode ser feita a partir da eliminação de um dos fatores, ou seja, a partir do emprego de agregados inertes ou de cimentos com baixos teores de álcalis ou isolamento da umidade. Na impossibilidade de eliminar um dos fatores, medidas preventivas devem ser tomadas para o emprego de agregados reativos em obras de construção civil. Entre essas, destacam-se a utilização de cimentos com baixos teores de álcalis ou a de cimentos com adições ativas mitigadoras da reação álcali-agregado: escória de alto-forno, cinza volante, metacaulim e sílica ativa, que foi o objeto de pesquisa do presente trabalho. No programa experimental foram analisados dois tipos de agregado potencialmente reativos com os hidróxidos alcalinos: EDVDOWR e PLORQLWR_ JUDQtWLFR. O primeiro, proveniente de rocha ígnea, tem como constituintes deletérios vidro, clorofeíta, calcedônia (sílica criptocristalina), que dará origem à reação do tipo iOFDOL_VtOLFD. O agregado milonito granítico provém de rocha metamórfica, tem como constituintes deletérios quartzo microgranular, quartzo recristalizado, quartzo com extinção ondulante e quartzo e feldspato deformados, que dará origem ao tipo de reação iOFDOL_VLOLFDWR. Com o objetivo de avaliar a eficiência de adições ativas em mitigar as reações, os agregados foram combinados com 16 cimentos com adições ativas. Escória de alto-forno foi adicionada a 15%, 30%, 45% e 60% e cinza volante, a 10%, 15%, 25% e 35%, teores normalmente encontrados nos cimentos brasileiros. Metacaulim foi adicionada a 5%, 10%, 15% e 20%, e sílica ativa, a 5%, 10% e 15%, teores representativos da faixa normalmente adicionada diretamente a concretos. Todos os materiais utilizados foram caracterizados química, física e mineralogicamente, incluindo a análise petrográfica dos agregados. As barras de argamassa foram analisadas ao MEV, microscópio óptico de luz transmitida, realizaram-se ensaios de porosimetria por intrusão de mercúrio e análises térmicas para quantificar a teor de portlandita residual, e determinou-se o teor de álcalis dentro das barras após a realização dos ensaios para verificar a migração de íons de sódio. Os resultados indicam que a eficiência das adições ativas varia de acordo com a composição química e mineralógica das adições, da proporção desse material no cimento, e do grau de reatividade do agregado.
Título en inglés
Effect of mineral admixtures in controlling the alkali-silica reaction and alkali-silicate reaction.
Palabras clave en inglés
Alkali-aggregate reaction
Basalt
Blast-furnace slag
Fly ash
Metakaolin
Milonite
Portland cement
Silica fume
Resumen en inglés
The alkali-aggregate reaction is a pathologic manifestation that can induce the premature distress and loss in serviceability of concrete structures affected. It is directly associated to the selection of materials (cement, coarse and fine aggregates, water and additives), as the interaction between these materials and environmental condition will grant the concrete some of the properties related to its service life. The slow reaction between alkali hydroxides soluble in the liquid phase within concrete pores and reactive aggregates gives rise to a gel that piles up within concrete voids and the aggregate-paste interface. In presence of water, the gel expands and exerts internal pressure in the concrete. When the internal pressure exceeds the tensile strength, cracking may come up as result. The alkali-aggregate reaction requires the action of water, reactive aggregate and alkalis altogether. Prevention can be carried out by eliminating one of these factors, i.e. employing either inert aggregates or lowalkali cements, or keeping the concrete away from moisture. Otherwise, preventive measures must be taken when reactive aggregates are used in civil construction works, such as the use of low-alkali cements or composite cements bearing alkaliaggregate- reaction mitigating admixtures: blast-furnace slag, fly ash, metakaolin and silica fume, which are the object of the present research. The experimental work included the analysis of two potentially reactive aggregates to alkali hydroxides: basalt and granite milonite. The igneous basalt carries deleterious constituents such as glass, chloropheite (cryptocrystalline silica), that will give rise to the DONDOL_VLOLFD type reaction while the metamorphic granite milonite carries micro granular, recrystallized, undulate-extinction-bearing quartz and deformed feldspar grains, that give rise to DONDOL_VLOLFDWH type reaction. Aiming at evaluating how efficient in mitigating these reactions the active admixtures are, these aggregates were mixed with 16 composite cements. The contents of admixtures followed those usually found in Brazilian industrial cements for blast-furnace slag (15%, 30%, 45%, 60%) and fly ash (10%, 15%, 25%, 35%), and those generally added directly to concrete for metakaolin (5%, 10%, 15%, 20%) and silica fume (5%, 10%, 15%). All materials were characterized for their chemical composition, physical properties and mineralogy. Petrography was carried out on the aggregates. The mortar bars were analyzed at the scanning electronic and transmitted-light optical microscopes. Mercury-intrusion porosimetry and thermal analyses were carried out to quantify residual portlandite. The alkali content within the bars was determined in order to verify migration of Na+ ions. The results show that the efficiency of active admixtures varies according to their chemical and mineralogical composition and proportioning in cement, and to the aggregate reactivity.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-02-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.