Disertación de Maestría
DOI
10.11606/D.3.2012.tde-16072013-112756
Documento
Autor
Nombre completo
Carlos Eduardo Carbone
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2012
Director
Tribunal
Pileggi, Rafael Giuliano (Presidente)
Betioli, Andrea Murillo
Cincotto, Maria Alba
Título en portugués
Pastas de cimento branco modificadas com diferentes tipos de látex.
Palabras clave en portugués
Cimento Portland estrutural branco
Estado endurecido
Estado fresco
Látex
Resumen en portugués
A adição de látex polimérico em argamassas usadas para reparos, argamassas colantes, argamassas técnica decorativas, argamassas de impermeabilização e chapiscos de alto desempenho é prática comum no setor de construção civil, visto que auxiliam seu desempenho no estado endurecido. As modificações do cimento Portland branco com diversos teores (de 5% a 20%) e tipos de látex (etileno vinil acetato, poliacetato de vinil versatato, estireno acrílico e estireno butadieno) resultaram em alterações no estado fresco (cinética de hidratação, cinética de consolidação, teor de ar incorporado) e no estado endurecido (resistência mecânica, elasticidade, absorção de água por capilaridade, permeabilidade ao ar e ao vapor), em muitos casos, proporcionais ao aumento de seus teores. Ao se atingir 20% de adição, em ralação à massa do cimento, houve ganhos expressivos no estado endurecido das pastas, como o aumento da resistência à tração na compressão diametral, e da resistência de aderência, diminuição do módulo elástico e da absorção de água por capilaridade sem comprometer a facilidade à permeabilidade do vapor. Todavia, no estado fresco não apresentaram condições de aplicação devido à excessiva fluidez e diminuição acentuada no processo de consolidação.
Título en inglés
Modified white cement pastes with different types of polymers.
Palabras clave en inglés
Fresh and hardened state
Latex
White Portland cement
Resumen en inglés
Modified Portland cement mortars have been used for repair, stickers, highperformance and finishing of facades is common practice in the construction industry, due his performance in hardened state. Additions of several latex levels (5% to 20%) and types (ethylene vinyl acetate, vinyl poliacetate versatate, styrene acrylic and styrene butadiene) resulted in changes in the fresh state (hydration kinetics, kinetic consolidation, air content) and hardened state (mechanical strength, elasticity, water absorption by capillarity, and steam permeability) and mostly the effects increase with the increase of its levels. When the Latex levels reached 20% in relation of cement were expressive gains in state hardened state, as increased tensile strength in diametral compression, and grip strength, decreased elastic modulus and water absorption by capillarity without compromising ease of vapor permeability. However, in the fresh state did not show application conditions due to the excessive fluidity and strong decrease in the consolidation process.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2013-07-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.