Disertación de Maestría
DOI
10.11606/D.3.2017.tde-18012017-142504
Documento
Autor
Nombre completo
Delver Plinio Estrada Caceres
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2016
Director
Tribunal
Cincotto, Maria Alba (Presidente)
Zampieri, Valdir Aparecido
John, Vanderley Moacyr
Título en español
Influencia del metacaolin en las propiedades en estado fresco del cemento Portland: hidratación y retracción química.
Palabras clave en español
Cimento Portland
Cinética química
Resistência dos materiais
Resumen en español
Actualmente los materiales cementicios suplementarios como el metacaolín, son comúnmente empleados en la industria cementera y de la construcción, debido a factores ambientales, económicos y técnicos. La mayoría de estudios que evalúan la influencia del metacaolín en sistemas cementicios, se enfocan en aspectos de desempeño y de resistencia mecánica, en edades avanzadas. Existen pocos estudios que evalúan la etapa inicial de hidratación. Por tanto, este trabajo tiene como propósito entender mejor la influencia que tiene la sustitución parcial de metacaolín en pastas de cemento Portland, durante las primeras 72 horas de hidratación. Normalmente para evaluar la cinética de hidratación se analiza el calor liberado, usando un calorímetro de conducción isotérmico. Sin embargo, otra técnica relativamente nueva usada en este estudio, es medir la retracción química en forma continua; en Brasil son raros los estudios que usen retracción química para obtener la cinética de hidratación. Para tal fin se elaboraron pastas utilizando reemplazos de metacaolín de 5, 10 y 20% en masa, además de una pasta de referencia, usando una relación constante agua/sólido de 0.5. La retracción química fue medida en forma continua automatizando el método de la dilatometría, también se evaluó la cinética de hidratación usando un calorímetro isotérmico. Adicionalmente, el desarrollo de los productos hidratados fue estudiado por análisis termogravimétrico y difracción de rayos X. Los resultados obtenidos muestran que existe una excelente relación entre la retracción química y la calorimetría y que la adición de metacaolín produce cambios en la cinética de hidratación, que también afectan a la retracción química.
Título en inglés
Influence of metakaolin in the fresh properties of Portland cement: hydration and chemical shrinkage.
Palabras clave en inglés
Chemical shrinkage
Hydration kinetics
Metakaolin
Portland cement
Resumen en inglés
Currently the supplementary cementitious materials such as metakaolin are commonly used in the cement and construction industry, due to environmental, economic and technical factors. Most studies evaluating the influence of metakaolin in cementitious systems focus on aspects of performance and mechanical strength at older ages. There are few studies evaluating the initial stage of hydration. Therefore, this paper aims to better understand the influence of the partial replacement of metakaolin in Portland cement pastes during the first 72 hours of hydration. Normally to evaluate the kinetics of hydration heat released is analyzed using an isothermal calorimeter. Nevertheless, another relatively new technique used in this study is to measure the chemical shrinkage continuously; in Brazil are rare studies using chemical shrinkage to obtain hydration kinetics. This study shows the influence of partial replacement of Portland cement by metakaolin in the hydration reactions and chemical shrinkage of cementitious pastes. For this, pastes were prepared using metakaolin replacements of 5, 10 and 20% by mass, and a reference paste, using a constant water/solid ratio of 0.5. Chemical shrinkage was measured continuously automating the method of dilatometry, hydration kinetics was evaluated using an isothermal conduction calorimetry. Additionally, the development of hydrated products was studied by thermogravimetric analysis and X-ray diffraction. The results show that there is an excellent relationship between chemical shrinkage and calorimetry and the addition of metakaolin leads to changes of the hydration kinetics, which also affect the chemical shrinkage.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-01-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.