Tesis Doctoral
DOI
Documento
Autor
Nombre completo
Vanderley Moacyr John
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1995
Director
Tribunal
Agopyan, Vahan
Cincotto, Maria Alba
Helene, Paulo Roberto do Lago
Kihara, Yushiro
Paulon, Vladimir Antonio
Título en portugués
Cimentos de escória ativada com silicatos de sódio.
Palabras clave en portugués
Cimentos
Escória de alto forno
Resumen en portugués
Os cimentos de escória apresentam boas possibilidades de mercado, especialmente em aplicações em que o cimento Portland não possa ser utilizado ou onde o seu uso provoque uma elevação dos custos. A confecção de matrizes para fibras sensíveis aos álcalis e a produção de cimentos com baixo calor de hidratação são exemplos. Neste trabalho, a escória foi ativada com silicato de sódio e cal hidratada. O ativador foi formulado de maneira a proporcionar teores de Na2O de 2,5% e 5%, SiO2 de 0% a 14,8% e Ca(OH)2 de 0%, 2,5% e 5%. O aumento dos teores de Na2O e de SiO2, dentro de determinados limites, propicia um notável crescimento da resistência à compressão. Este crescimento da resistência está associado a uma diminuição da porosidade, para um mesmo fator/água aglomerante. Certamente a diminuição da porosidade é devida a um menor grau de organização cristalina dos produtos hidratados, decorrente do aumento da velocidade de precipitação de hidratados e de gel de N-C-S-H. A adição de Ca(OH)2 diminui a velocidade de perda da trabalhabilidade. Os cimentos de escória ativada com silicatos de sódio podem apresentar resistência à compressão de até 100 MPa, superior à dos cimentos Portland, com calor de hidratação da mesma ordem de grandeza. A velocidade de carbonatação destes cimentos é equivalente a dos cimentos Portland de mesma resistência. No entanto, estes cimentos apresentam maior retração hidráulica.
Título en inglés
Sodium silicate activated blast furnance slag cements.
Palabras clave en inglés
Blast furnace slag
Cement
Resumen en inglés
Binders based on ground granulated blast furnace slag (BFS) are suitable for the building industry, mainly if the use of Portland cement is expensive or may cause problems, such as: alkali sensitive fibre-reinforced cement and concretes and low heat-hydration concretes. BFS is activated by sodium silicates and hydrated lime. The compound's proportions are: Na2O - 2.5 and 5.0%; SiO2 from 0 to 14.8%; CaOH2 - 0, 2.5 and 5%. The increase of Na2O and SiO2 amounts allows a considerable improvement of binder strength, with values up to 100 MPa. This increase of the strength is related to the decrease of the porosity for a constant water-binder ratio. The porosity is affected certainly by the reduction of the degree of cristalynity of the hydrated compounds, due to the increase of the speed of precipitation of the hydrates or the N-C-S-H gel. It is possible to obtain BFS binders stronger than the Portland cement, with similar hydration heat. The carbonation rate of these new binders is equivalent to those of Portland cement specimens with similar strength. However these BFS binders have higher drying shrinkage.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-10-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.