Tesis Doctoral
DOI
10.11606/T.3.2007.tde-28032008-174009
Documento
Autor
Nombre completo
Antônio Acacio de Melo Neto
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2007
Director
Tribunal
Cincotto, Maria Alba (Presidente)
Figueiredo, Antonio Domingues de
Isaia, Geraldo Cechella
John, Vanderley Moacyr
Repette, Wellington Longuini
Título en portugués
Influência de aditivos redutores e compensadores de retração em argamassas e pastas com cimento de escória ativada.
Palabras clave en portugués
Ativação alcalina
Cimento de escória
Escória de alto forno
Retração
Resumen en portugués
O objetivo desta tese foi o estudo da influência do aditivo redutor de retração (SRA) e o aditivo compensador de retração (SCA) em argamassas e pastas de cimento de escória ativada com silicato de sódio. A metodologia foi centrada na análise da retração por secagem e autógena, com o estudo de outras características que influenciam no fenômeno da retração, como as propriedades mecânicas. Para o avanço no conhecimento do efeito dos aditivos no comportamento do cimento de escória, foi caracterizada a microestrutura com a determinação da análise por termogravimetria, porosimetria e difração de raios X. Neste estudo foram empregados os seguintes teores de aditivo, porcentagem relativa à massa de aglomerante: 0,5%, 1%, 1,5% e 2% do aditivo SRA e 5%, 10% e 15% do aditivo SCA. Para a análise da influência da relação a/agl foram empregadas três teores: 0,40, 0,48 e 0,56. No estudo das amostras de referência, sem a utilização de aditivo, observou-se que o aumento da relação a/agl causa o aumento da retração por secagem e da retração autógena do cimento de escória ativada. A diminuição da resistência mecânica com o aumento da relação a/agl, o que torna o esqueleto sólido mais susceptível à deformações, e o aumento das tensões capilares, em razão do aumento da quantidade de água livre para ser evaporada, são os principais fatores para o aumento da retração por secagem. No caso da retração autógena, seu aumento é atribuído ao aumento da auto-secagem com o aumento do volume de poros com diâmetro na faixa de mesoporos, além da diminuição da resistência mecânica. O aditivo redutor de retração (SRA) conseguiu reduzir a retração por secagem em percentuais de 40% até 74% aos 28 dias, no entanto, este tipo de aditivo não obteve êxito no combate a retração autógena. Com relação à resistência mecânica, o aditivo SRA causou a redução de até 40%, efeito atribuído à diminuição do grau de hidratação e retardo do refinamento da porosidade. O aditivo compensador de retração (SCA) amenizou a retração por secagem e a retração autógena, reduzindo em até 64% e 70%, respectivamente, porém reduziu em até 60% a resistência mecânica do cimento de escória ativada. Com relação à microestrutura, o aditivo SCA diminuiu o grau de hidratação e aumentou a porosidade total, com o aumento da proporção do volume de macroporos.
Título en inglés
Effect of shrinkage compensating and reducing admixtures in alkali activated slag mortars and pastes.
Palabras clave en inglés
Alkali activated
Blast furnace slag
Microstructure
Shrinkage compensating admixture (SCA)
Shrinkage reducing admixture (SRA)
Resumen en inglés
The aim of this research was the study of the influence of shrinkage reducing admixture (SRA) and shrinkage compensating admixture (SCA) in mortars and pastes of blast furnace slag activated with sodium silicate. The method was centered in the analysis of free drying and autogenous shrinkage, with other characteristics that affect the shrinkage, as the mechanical properties. The microstructure behavior was accomplished with thermogravimetry (TG), mercury intrusion porosimetry (MIP) and X-ray diffraction (XRD). The samples were prepared with 0,5%, 1%, 1,5% and 2% of SRA admixture and 5%, 10% and 15% of SCA admixture, by binder mass. The effect of water/binder ratio was accomplished in three contents: 0,40, 0,48 and 0,56. In the reference mixtures, without admixtures, it was observed that an increase of water/binder ratio incurs in an increase of drying and autogenous shrinkage of alkali activated slag. The explanations for drying shrinkage behavior are the decrease of mechanical strength as consequence of water/binder increase, that turns the porous structure more susceptible to deformations, and the increase of the capillary tensions, attributed to the increase of free water to be evaporated. The increase of autogenous shrinkage with water/binder ratio is attributed to the increase of pore volume with diameter in the mesopores range, besides the decrease of the mechanical strength. The shrinkage reducing admixture (SRA) diminish drying shrinkage of 40% up to 74% at 28 days, however, this type of admixture was not capable to combat the autogenous shrinkage. About mechanical strength, the SRA admixture incurs in a decrease up to 40% of compression strength that it was attributed to the decrease of the hydration degree and retard of pore size refinement. The shrinkage compensating admixture (SCA) softened drying and autogenous shrinkage, reducing in up to 64% and 70%, respectively. However, the SCA admixture decreases in up to 60% mechanical strength of alkali activated slag. About microstructure, SCA admixture reduced the hydration degree and it increased the total porosity, with the increase of macropores volume.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2008-04-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.