Master's Dissertation
DOI
10.11606/D.3.2016.tde-09122016-102952
Document
Author
Full name
Tiago Gonçalves Goto
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2016
Supervisor
Committee
Moreira, José Roberto Simões (President)
Mourão, Marcelo Breda
Oliveira, Fábio Branco Vaz de
Title in Portuguese
Estudo experimental do processo de oxidação do ferro com vapor de água para a produção de gás hidrogênio.
Keywords in Portuguese
Ciclos termoquímicos
Combustível solar
Ferro
Hidrogênio
Oxidação
Abstract in Portuguese
Neste trabalho, foi estudado a oxidação do ferro com vapor d'água em forno elétrico, para a produção de gás hidrogênio. Partindo-se da revisão bibliográfica, escolheu-se o ferro devido suas propriedades e por apresentar um bom rendimento, além disso o ferro é um material barato e abundante. Na estudo experimental foi três experimentos diferentes. No primeiro, o ferro foi oxidado em forno elétrico em temperaturas de 600 a 1000ºC, variando a cada 100ºC, e tempo fixado em 3 horas. Na segunda série de experimento, foi fixado a temperatura em 800ºC e variou a duração do processo de oxidação de 1 a 4 horas, com variação de 1 hora. E na terceira série de experimentos foi realizado a análise termogravimétrica para avaliação da cinética química do processo de oxidação. Os resultados dos experimentos indicaram a produção de gás hidrogênio em quantidades maiores em temperatura de 1000ºC. Além disso foi possível observar que a taxa de oxidação do ferro é maior durante a primeira hora de ensaio. A estimativa de hidrogênio produzido é de 0,9549 g/min -m2 em oxidação a 1000ºC. Já nos resultados da termogravimetria foi obtido a energia de ativação de 147 kJ/mol.
Title in English
Experimental study of iron oxidation process with water vapor to produce hydrogen gas11.
Keywords in English
Hydrogen
Iron oxidation
Solar fuel
Thermochemical cycle
Abstract in English
In this work was studied the oxidation of iron by steam in the electric furnace to produce hydrogen. The first step was the literature review and iron oxide was chose to be oxidized, due to its characteristics and good yield. Furthermore, the iron is a cheap and abundant in the earth. In the experimental studies was conducted three different experiments. The First one, the iron was oxidized in the electric furnace in the temperature range of 600 - 1000ºC with a variation of 100ºC and the oxidation time was fixed in 3 hours. The second experiment was conducted with fixed temperature of 800ºC and varied the oxidation time, the range of time was from 1 to 4 hours with a variation of 1 hour. The third experiment was the thermogravimetric analysis to study the chemical kinetics, with three different temperature, 600, 800 and 1000ºC. The result of studies showed that a high temperature the hydrogen production increased and decreased with low temperature. Furthermore, the high oxidation rate was observed in the first hour of the experiment. The hydrogen production was estimated in 0.9549 g/min - m2 at 1000ºC. Another result was the activation energy Ea= 147 kJ/mol.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-12-09
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.