• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Mémoire de Maîtrise
DOI
10.11606/D.3.2009.tde-01072009-145404
Document
Auteur
Nom complet
Adalto de Farias
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2009
Directeur
Jury
Batalha, Gilmar Ferreira (Président)
Abrao, Alexandre Mendes
Coelho, Tarcisio Antonio Hess
Titre en portugais
Análise da tensão residual e integridade superficial no processo de torneamento em material endurecido do aço ABNT 8620 cementado.
Mots-clés en portugais
Acabamento de superfícies
Difração por raios-X
Tensão residual
Torneamento
Usinagem
Resumé en portugais
Este trabalho tem a intenção de contribuir com informações sobre a integridade superficial resultante do processo de torneamento em material endurecido de componentes mecânicos fabricados em aço cementado ABNT 8620 (DIN 21 NiCrMo 2). A análise das tensões residuais do corpo de prova foi experimentalmente conduzida pelo Método do Furo Cego Incremental, no qual um pequeno furo é introduzido na superfície do componente e a deformação aliviada é registrada por meio de extensômetros especiais, e também, pelo método da difração de raios-X. A superfície foi analisada através de parâmetros obtidos do mapeamento tridimensional da topografia superficial com instrumento de interferometria laser. Os parâmetros de rugosidade, selecionados para medição, visaram uma caracterização funcional das superfícies obtidas, tais como capacidade de carga, capacidade de retenção de fluidos lubrificantes e resistência ao desgaste. Também foram executados ensaios metalográficos para avaliar a existência de camadas de material alteradas abaixo da superfície. Os resultados indicaram que o torneamento em material endurecido foi capaz de produzir uma superfície resultante com boa área de contato, boa capacidade de carregamento e razoável capacidade de retenção de fluidos uma vez que nem todos os parâmetros se encontraram na faixa funcional ideal. O torneamento em material endurecido induziu tensão de compressão nas camadas das amostras cementadas, cuja condição original era tensão residual de tração. Não foram detectadas alterações expressivas na camada cementada, principalmente na região limítrofe da área transversal com a superfície devido ao aquecimento e rápido resfriamento imposto pelo processo de usinagem.
Titre en anglais
Residual stresses and surface integrity analysis after hard turning process of case hardened steel ABNT 8620.
Mots-clés en anglais
3-D roughness
Blind hole method
Case hardened steel
Hard turning
Residual stress
Surface integrity
White layers
X-ray diffraction
Resumé en anglais
The aim of the present work is to provide relevant information regarding the obtained surface integrity during hard turning process of mechanical components manufactured from case hardened steel ABNT 8620 (DIN 21 NiCrMo 2). The sample residual stress analysis has been experimentally conducted by the incremental Blind Hole method, in which a small hole is machined on the surface of the component and the relieved deformation is recorded through special strain gages, and by the X-ray diffraction technique. The surface was examined by parameters obtained from the surface topography three-dimensional mapping with a laser interferometer instrument. The selected roughness parameters analysis intends to have a functional characterization such as bearing capacity, fluid and lubricants retention ability and contact wear resistance. In the search for altered material layers beneath the surface, metallographic studies were carried out. The functional bearing area curve analysis parameters indicated that the resulting surface has a good area contact, good bearing capacity and reasonable ability to fluid retention as the reduced valley depth parameter did not produced negative values for all conditions tested. The hard turnig process was able to add compression residual stress condition at the surface, and no significant changes were found at the case hardened layer due to rapid heating and cooling imposed by the hard turning process.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2009-07-07
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.