Mémoire de Maîtrise
DOI
10.11606/D.3.2018.tde-06092018-090428
Document
Auteur
Nom complet
Larissa Mitie Ihara
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2018
Directeur
Jury
Tanaka, Deniol Katsuki (Président)
Pintaúde, Giuseppe
Tschiptschin, Andre Paulo
Titre en portugais
Caracterização de fratura por fadiga em componentes mecânicos.
Mots-clés en portugais
Barra estabilizadora
Engrenagens
Fadiga dos materiais
Mecânica da fratura
Resumé en portugais
Esta Dissertação, submetida à Escola Politécnica da Universidade de São Paulo, tem como objetivo a caracterização de fratura por fadiga em componentes mecânicos. Esse estudo foi motivado por dois casos de falha: barras estabilizadoras de truques de trem para transporte de minério, e engrenagens de redutores de grande porte, aplicados em turbogeradores em usinas de cogeração. Foi apresentada uma revisão da literatura sobre nucleação e propagação de trincas de fadiga, sobre fadiga de contato e por flexão de dentes, os dois principais modos de falha de engrenagens, e sobre a dinâmica do truque de trem. As amostras coletadas de barras falhadas foram caracterizadas e suas superfícies de fratura foram examinadas. A trinca de fadiga iniciou-se em uma das dobras do rebaixo, em local com dano por corrosão, que favoreceram sua nucleação. Uma análise por elementos finitos foi realizada para analisar as tensões residuais devido ao processo de dobra da barra e conformação do rebaixo e as tensões devido à operação, num caso crítico de warp tracionando a barra. Os resultados mostraram que localmente a tensão de escoamento do material foi superada, especialmente nas regiões de pequeno raio de curvatura devido ao rebaixo. Para o caso das engrenagens, foi feita uma análise de confiabilidade por distribuição de Weibull com base nos tempos de vida dos componentes falhados e do restante fabricado. Do resultado inferiu-se que as falhas consistiram na "mortalidade infantil" dos componentes. Havia apenas uma amostra de engrenagem falhada disponível para análise, a qual foi detalhadamente caracterizada e cuja superfície de fratura foi minuciosamente estudada, a fim de determinar o modo e o mecanismo de falha, o início da trinca e, com isso, a causa da falha. Pôde-se concluir que a engrenagem falhou devido a fadiga por flexão de dente devido a um desalinhamento na montagem. Determinadas as causas das falhas, podem-se sugerir soluções, aumentando assim a confiabilidade dos componentes. As sugestões podem dizer respeito ao próprio projeto, à seleção de materiais, aos processos de fabricação, ao tratamento térmico, à montagem, ou ao sistema de lubrificação.
Titre en anglais
Characterization of fatigue failure in mechanical components.
Mots-clés en anglais
Failure analysis
Fatigue
Frame brace
Gears
Mechanical engineering
Resumé en anglais
This Dissertation, submitted to the Escola Politécnica da Universidade de São Paulo, aims to characterize fatigue fracture in mechanical components. This study was motivated by two cases of failure: frame brace of train bogies for ore transportation, and gears of large transmission systems, applied to turbogenerators in cogeneration power plants. A literature review was presented on nucleation and propagation of fatigue cracks, contact and tooth bending fatigue, which are the two main modes of failure of gears, and train bogie dynamics. Samples collected of failed bars were characterized and their fracture surfaces were examined. The fatigue crack initiated at one of the bends of the "fillister", where corrosion damage took place - both of which favoured the nucleation. A finite element analysis was performed to analyze the residual stresses due to the bending process of the bar and the forming of the "fillister" and the stresses due to operation, in a critical case of warp tensioning the bar. The results showed that locally the yield stress of the material was exceeded, especially in the regions of small radius of curvature due to the "fillister". For the case of the gears, a reliability analysis was performed by Weibull distribution based on the lifetimes of the failed components and the remainder manufactured. From the result it was inferred that the failures consisted of the "infant mortality" of the components. Only one failed gear sample was available for the analysis, which was thoroughly characterised and whose fracture surface was minutely studied, in order to determine the mode and mechanism of failure, crack initiation and, hence, cause of failure. It was concluded that the gear failed due to tooth bending fatigue due to misalignment in the assembly. Having determined the causes of failures, solutions can be suggested, thus increasing the reliability of the components. Suggestions may concern the design itself, materials selection, manufacturing processes, heat treatment, assembly, or lubrication system.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2018-09-06
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.