Tesis Doctoral
DOI
10.11606/T.3.2016.tde-08072016-151235
Documento
Autor
Nombre completo
Gil Magno Portal Chagas
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2015
Director
Tribunal
Machado, Izabel Fernanda (Presidente)
Barbosa, Patrícia Alves
Coelho, Reginaldo Teixeira
Silva, Marcio Bacci da
Souza, Roberto Martins de
Título en portugués
Estudo do processo de formação do cavaco durante o torneamento e sua relação com a microestrutura utilizando o método dos elementos finitos.
Palabras clave en portugués
Aço inoxidável
Microestrutura
Simulação numérica
Torneamento
Usinagem
Resumen en portugués
O objetivo desse trabalho foi avaliar o processo de formação do cavaco durante o torneamento utilizando simulação numérica pelo método dos elementos finitos. Para realizar o estudo foram definidos dois tipos de aços inoxidáveis austeníticos, um com matriz metálica sem a presença significativa de inclusões, do tipo ABNT 304, e outro com a presença de inclusões não metálicas, do tipo ABNT 303. O estudo foi focado nos mecanismos de formação e ruptura do cavaco, na determinação das forças de usinagem, no campo de tensões, deformações, e temperaturas durante o processo, que foram relacionados com aspectos e características da microestrutura do material. Os resultados obtidos foram comparados com as forças de usinagem experimentais, com a espessura e morfologia do cavaco. O desenvolvimento do trabalho, de acordo com a metodologia adotada, foi realizado em diferentes etapas. Inicialmente foi elaborado e aplicado um modelo de simulação da usinagem considerando o material homogêneo. Em outra etapa, foi realizada a modelagem de uma microestrutura submetida a um estado de tensão e deformação semelhante ao encontrado na simulação da usinagem realizada com material homogêneo. Os resultados mostraram que as partículas das inclusões maiores, alongadas, e em maior quantidade aumentam a tensão e a deformação na microestrutura. As elevadas temperaturas obtidas na usinagem dos aços inoxidáveis austeníticos aumentam a ductilidade dos sulfetos, esses se deformam em compressão junto com a matriz, e têm um efeito limitado como agente de redução dos esforços de usinagem. Por outro lado, os sulfetos facilitam a etapa de ruptura do cavaco em tensões trativas, e tendem a se romper facilitando o processo de quebra.
Título en inglés
Study of the formation process during machining and its relationship with the microstructure using finite element method.
Palabras clave en inglés
Machining
Microstructure
Numerical simulation
Stainless steel
Turning
Resumen en inglés
The aim of this study was to evaluate the chip formation process during turning using a numerical simulation by finite element method. Two different austenitic stainless steel were evaluated, one without a significant presence of inclusions, ABNT 304, and another one with the presence of non-metallic inclusions, ABNT 303. The study was focused on the chip formation and rupture, in determining the machining forces, stresses, strains and temperatures during the process, which were related to aspects and characteristics of the microstructure. The results obtained were compared with the experimental machining forces, thickness and morphology of the chip. The development of the work, according to the methodology, was carried out at different steps. The first one implemented a simulation model considering a homogeneous material. In the next step, the microstructure was subjected to a state of stress similar to that found in the simulation of the machining performed with homogeneous material. The results showed that the largest inclusion particles, elongated and in greater quantity, increase stresses and strains in the microstructure. The high temperatures obtained when machining austenitic stainless steel increase the ductility of sulfides. These are deformed in compression along with the matrix, and have a limited effect in reducing machining forces. On the other hand, sulfides facilitate the chip fracture at tensile stresses.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-07-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.