Disertación de Maestría
DOI
10.11606/D.3.2011.tde-09122011-105117
Documento
Autor
Nombre completo
Cristiano Fernandes Lagatta
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2011
Director
Tribunal
Souza, Roberto Martins de (Presidente)
Adamowski, Júlio Cezar
Recco, Abel André Cândido
Título en portugués
Medição de tensões residuais em filmes finos durante o processo de deposição.
Palabras clave en portugués
Filmes finos
Medição in-situ
Nitreto de titânio
Tensões residuais
Triodo magnetron sputtering
Resumen en portugués
Neste trabalho foram realizadas algumas deposições de filmes de Nitreto de Titânio sobre substrato de aço inoxidável. Foi utilizado o processo conhecido como triodo magnetron sputtering. Os parâmetros de deposição foram mantidos entre as deposições, exceto pela voltagem de bias no substrato, que foi variada de uma deposição para outra. Medições in-situ das tensões residuais no filme depositado foram realizadas. As medições foram feitas através do método da curvatura do substrato, utilizando-se um sensor capacitivo posicionado dentro da câmara de deposição. Embora o dispositivo não tenha sido capaz de quantificar os valores de tensão, foi possível identificar a natureza das mesmas, indicando se elas são de caráter trativo ou compressivo. Comprovou-se a possibilidade do uso de sistemas capacitivos para medições em sputtering. Observou-se que os filmes depositados apresentaram tensões de caráter trativo durante as deposições.
Título en inglés
Thin films residual stress measurement during deposition process.
Palabras clave en inglés
In-situ measurement
Residual stress
Thin films
Titanium nitride
Triode magnetron sputtering
Resumen en inglés
In this work, a series of depositions of titanium nitride thin films was conducted in a triode unbalanced magnetron sputtering chamber. Similar parameters were selected during each deposition, except for the substrate bias voltage, which was different for every deposition. An in-situ measurement of film residual stresses was carried out as the depositions proceeded. This measurement was based on substrate curvature, which was assessed by a home-built capacitive sensor positioned inside the sputtering chamber. Although the measurement device was not able to quantify the stress values, it was possible to identify if they were tensile or compressive. It was proved the possibility of using capacitive measurement devices in sputtering processes. It was possible to observe that the films underwent tensile stresses during the deposition.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-12-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.