Tesis Doctoral
DOI
10.11606/T.3.2008.tde-11052009-174233
Documento
Autor
Nombre completo
Carlos Eddy Valdéz Salazar
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Padovese, Linilson Rodrigues (Presidente)
Capó Sánchez, Julio Antonio
Delijaicov, Sergio
Hioki, Daniel
Stipkovic Filho, Marco
Título en portugués
Avaliação através da inspeção magnética da condição superficial de anéis de rolamento de aço DIN 100Cr6 após torneamento duro a seco.
Palabras clave en portugués
Ensaios magnéticos não destrutivos
Processos de fabricação
Ruído magnético de Barkhausen
Tensão residual
Resumen en portugués
O presente trabalho visa apresentar informações que viabilizem a fabricação de componentes de rolamentos com limites superiores de resistência à fadiga, com a intenção de proporcionar uma vida útil maior ao rolamento, e, também, a otimização da fabricação das peças, dispensando em alguns casos o processo final e usual de retificação, o que implica uma redução de custos. As motivações deste estudo são a geração de altas tensões residuais compressivas no torneamento duro-seco a altas velocidades, a aplicação do RMB como técnica de medição das tensões residuais em aço 100CrMn6 e a otimização da qualidade/custos na fabricação de rolamentos. Para atingir essas metas, será estudada a influência dos parâmetros da usinagem (velocidade de corte (Vc), avanço (a), penetração (p) e desgaste da ferramenta (VB)) na geração das tensões residuais superficiais (sR) e sobre as forças de torneamento (Fc, Fa, Fp), em anéis internos de rolamentos cônicos de aço DIN 100CrMn6 endurecidos termicamente, procurando-se estabelecer uma correlação entre o desgaste da ferramenta e os referidos esforços e tensões residuais. Na etapa experimental, será utilizado um planejamento fatorial completo para executar os ensaios e medições projetadas. No ensaio de torneamento, serão medidas as forças de corte utilizando-se, para isso, um dinamômetro piezoelétrico. Em seguida, serão efetuadas medições de rugosidade. Também será realizado o estudo da microestrutura através da análise metalográfica. As tensões residuais serão medidas utilizando-se o método do furo-cego com extensometria elétrica, e as medidas das alterações microestruturais superficiais serão realizadas pela técnica do Ruído Magnético de Barkhausen (RMB). Serão correlacionados os valores de tensão residual obtidos pela técnica do furo com o RMB.
Título en inglés
Evaluation through the mgnetic inspection of the superficial condition of steel bearing rings DIN 100Cr6 after hard and dry turning.
Palabras clave en inglés
Hard turning
High speed turning
Machining forces
Magnetic Barkhausen noise
Residual stress
Tool wear
Resumen en inglés
The present work presents information for the manufacturing of ball bearings components with higher limits of resistance to fatigue, enabling a longer useful life and also the optimization of the production of the pieces, making the usual and final process of grinding unnecessary, which would result in a costs reduction. The motivations of this study are the generation of compressive high residual stress in the hard-dry turning at high speeds, the application of the MBN as technique of measurement of the residual stress in steel 100CrMn6, and the optimization of the quality/costs in the manufacturing of ball bearings. In order to achieve these purpose, the work will study the influence of the machining parameters (cutting speed (Vc), feed rate (a), depth of cut (p), and wear of tool (VB)) in the generation of the superficial residual tensions and also the turning forces (Fc, Fa, Fp), in internal conical rings of ball bearings of steel 100CrMn6 thermally hardened, seeking to find a correlation between the stress of the tool and the referred efforts. In the experimental phase, a complete factorial planning will be used to perform the tests and measurements projected. In the turning tests, the cutting forces will be measured using a piezoelectric dynamometer. After that, measurements of superficial roughness will be performed. Also, the study of the microstructure will be made through the metallographic analysis. The residual tensions will be measured using the strain gage hole-drilling method and the measurement of the superficial microestrutural alterations will be carried out using the technical of the magnetic Barkhausen noise (MBN). The values of residual tension obtained by the hole-drilling will be correlated with the RMB.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Tese_Carlos.pdf (14.10 Mbytes)
Fecha de Publicación
2009-07-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.