Thèse de Doctorat
DOI
10.11606/T.3.2008.tde-11112008-104640
Document
Auteur
Nom complet
Vanderlei Ferreira
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2008
Directeur
Jury
Sinatora, Amilton (Président)
Bressiani, Ana Helena de Almeida
Godoy, Geralda Cristina Durães de
Mello, José Daniel Biasoli de
Yoshimura, Humberto Naoyuki
Titre en portugais
Ultra-baixo coeficiente de atrito entre o par cerâmico Si3N4-Al2O3 em água.
Mots-clés en portugais
Água
Alumina
Atrito
Cerâmica
Lubrificação
Rugosidade superficial
Resumé en portugais
Neste trabalho, foi investigado o comportamento tribológico dos pares cerâmicos aluminanitreto de silício no deslizamento em água e em uma suspensão de sílica coloidal em água (hidrosol). O objetivo foi verificar a possibilidade de atingir um coeficiente de atrito da ordem de unidades de milésimos, aqui chamado de ultra-baixo coeficiente de atrito (UBCA), verificar se a mudança do meio, de água para hidrosol, diminui o running-in do coeficiente de atrito, e verificar o efeito da variação da rugosidade inicial da alumina no comportamento do atrito. Os ensaios foram realizados na configuração de teste esferasobre- disco, no qual a esfera foi de nitreto de silício e o disco de alumina, sob carga normal de 54 N e velocidade de 1 m/s. A água utilizada nos ensaios foi destilada e deionizada, e a sílica coloidal amorfa, hidrofílica, sem porosidade e de tamanho médio de partícula de 12 nm foi a Aerosil® 200, e o hidrosol foi preparado com pH 8,5 num eletrólito de NaCl de 1 mM. A esfera de nitreto de silício, adquirida comercialmente, e a alumina, sinterizada em laboratório, foram caracterizadas quanto a densidade, as fases foram determinadas por difração de raios X, microscopia eletrônica de varedura (MEV) observada em amostras ceramográficas atacadas. Algumas propriedades mecânicas como dureza, módulo de elasticidade e tenacidade à fratura foram determinadas. Duas condições de rugosidade dos discos de alumina foram utilizadas nos ensaios tribológicos, 350 nm e 10 nm RMS. Em todos os ensaios, em água, em hidrosol e independentemente da rugosidade inicial do disco o coeficiente de atrito no regime permanente apresentou pequena dispersão de valores de 0,002 a 0,006, e não foi possível estabelecer diferença entre elas. A menor rugosidade do disco de alumina acarretou menor desgaste e menor período de running-in de coeficiente de atrito, tanto em água quanto em hidrosol. Os ensaios em meio de hidrosol acarretaram menor desgaste das cerâmicas e apresentaram menor running-in de coeficiente de atrito, comparados aos ensaios com água. O disco de alumina apresentou menor desgaste do que a esfera de nitreto de silício, em todas as condições estudadas. Com a análise das perdas volumétricas, da rugosidade final das superfícies desgastadas, das curvas de coeficiente de atrito e das espessuras mínimas de filme lubrificante, calculadas com uso de modelo da literatura, foi possível relacionar a diminuição do desgaste e do running-in de coeficiente de atrito em meio de hidrosol, com a presença da sílica na superfície ou próxima dela.
Titre en anglais
Ultra-low friction coefficient between Si3N4-Al2O3 in water.
Mots-clés en anglais
Alumina
Ceramic
Hydrosol
Silicon nitride
Surface roughness
Ultra-low friction
Water
Water lubrication
Resumé en anglais
In this work, the tribological behavior of the alumina-silicon nitride couple was investigated under water and hydrosol (colloidal silica suspensions in water) lubricated sliding. The purposes were to study how an ultra-low friction coefficient can be achieved and to analyze the effects of the environment, lubricant and alumina roughness changes on the friction behavior. Ball-on-disk tests with a normal load of 54 N and a sliding speed of 1 m/s were carried out, using a silicon nitride ball and an alumina disk. The water used as lubricant was distilled and deionized. The silica was amorphous colloidal and hydrophilic, without porous and with a 12 nm medium particle diameter, commercially named Aerosil ® 200. The hydrosol was obtained with a pH value of 8,5 and a 1mM NaCl electrolyte. To estimate the minimum film thickness, formed during the lubricated sliding tests, a theory model was used. The commercial silicon nitride balls and the alumina disks, which were conformed and sintered in laboratory, were characterized by density, X-ray diffraction and scanning electron microscopy measurements. The mechanical properties such as hardness, Young modulus and fracture toughness were determined. The friction coefficient values obtained in the steady state regime showed low standard deviations (0,002 to 0,006) under all conditions. A shorter period of running-in was observed with the lower disk roughness, both in water and hydrosol lubrication. The hydrosol lubricated sliding produced a lower wear and friction running-in comparing with the tests under water lubrication. The alumina disk always showed lower wear than the silicon nitride ball. The volume loss, friction coefficients, worn surfaces roughness and minimum film thickness results suggest that the wear and friction coefficient running-in decrease was caused by the presence of silica on the sliding surfaces or on the near surface regions.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
TeseVFerreira.pdf (5.95 Mbytes)
Date de Publication
2008-12-12
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.