• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Thèse de Doctorat
DOI
10.11606/T.3.2016.tde-14072016-113733
Document
Auteur
Nom complet
Luiz Alberto Pereira das Neves Franco
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2015
Directeur
Jury
Sinatora, Amilton (Président)
Albertin, Eduardo
Murray, Henara Lilian Costa
Silva, Carlos Henrique da
Souza, Roberto Martins de
Titre en portugais
Abrasão de ferro fundido cinzento: aplicação a motores automotivos.
Mots-clés en portugais
Abrasão
Automóveis
Camisa
Cilindro
Coeficiente de atrito
Ferro fundido cinzento
Grafitas
Resumé en portugais
Uma parte significativa das perdas por atrito num motor automotivo resulta da ação de partículas abrasivas. Dentre as fontes possíveis, podem ser citados o próprio meio ambiente - partículas que passam pelo filtro de ar - o desgaste de partes metálicas do motor ou mesmo resíduos de combustão. Essas partículas podem ficar encrustadas em anéis do pistão, ou ficar na interface entre pistão e bloco ou camisa, e são responsáveis por sulcos axiais, na direção do movimento do pistão, observáveis em motores usados. O objetivo deste trabalho foi obter um melhor entendimento dos mecanismos de desgaste relacionados com o sulcamento de camisa/bloco e identificar conjuntos de testes laboratoriais capazes de reproduzi-los sob condições controladas. Amostras de ferro fundido cinzento (FoFo) e de aço AISI 1070 com dureza de matriz próxima daquela encontrada em FoFo (?200HV30) foram submetidas a ensaios de riscamento em tribômetros. Verificou-se que riscos executados com um endentador cônico submetido a cargas na faixa de 20 a 50 mN eram similares aos sulcos observados em camisas ou blocos. Ensaios com outros materiais, como alumínio e latão e mesmo aço de diferentes durezas contribuíram para melhorar o entendimento dos resultados. Não foi observada transição brusca entre mecanismos de abrasão. O cálculo do fator de remoção de material, fab, a partir de perfilometria óptica resultou em valores com dispersão elevada; não foi possível associa-los aos diferentes mecanismos de abrasão observados. Valores obtidos para o coeficiente de atrito no riscamento permitiram fazer uma estimativa inicial de energia gasta nos processos abrasivos do motor.
Titre en anglais
Abrasion of gray cast iron: application to automotive engines.
Mots-clés en anglais
Abrasion
Coefficient of friction
Cylinder
Graphite
Gray cast iron
Liner
Resumé en anglais
A significant part of the friction losses in an automotive engine results from the abrasive action of particles. Among possible sources of such particles one can mention the environment - particles that were not retained by the filters - metallic residues from worn parts or even combustion residues. They may be picked up by piston rings and become part of their surfaces or stay loose in the piston/liner interface. Those particles are responsible for axial grooves that are observed in the liners of used engines. The objective of this work was to get a better understanding of the wear mechanisms related to liner/bore grooving and to identify a laboratory testing setup that might reproduce them under controlled conditions. Specimens of Gray Cast Iron (GCI) and of AISI 1070 steel with matrix hardness close to that found in GCI (?200HV30) were submitted to scratch tests in a tribometer. It was found that scratches performed under 20-50 mN indenter load (conical tip) were similar to grooves observed in cylinder liners. Tests with other materials such as aluminum, brass and even steel with different hardness values contributed to a better understanding of the results. No sharp transition between abrasion mechanisms was observed. Calculation of material removal factor fab from optical profilometry resulted in values with a large dispersion; they could not be associated with different abrasion mechanisms. Friction coefficient values obtained from the tests were used to make preliminary estimates of energy consumption due to abrasive processes in the engine.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-07-15
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.