Mémoire de Maîtrise
DOI
10.11606/D.3.2012.tde-19112012-122615
Document
Auteur
Nom complet
Roberto Pereira de Oliveira
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2012
Directeur
Jury
Sinatora, Amilton (Président)
Genova, Luís Antonio
Scandian, Cherlio
Titre en portugais
Ultra baixo coeficiente de atrito no deslizamento de  Al2O3 - Si3N4: efeito das variáveis químicas (pH e concentração de sílica coloidal).
Mots-clés en portugais
Água
Alumina
Atrito
Cerâmica
Desgaste
Nitreto de silício
Ultra baixo coeficiente de atrito
Resumé en portugais
O objetivo deste trabalho, foi investigar o comportamento tribológico do par cerâmico alumina - nitreto de silício no deslizamento em água com pH controlado e em uma suspensão com diferentes concentrações de sílica coloidal em água, e verificar a possibilidade de atingir um coeficiente de atrito da ordem de milésimos (μ < 0,01), aqui chamado de ultra baixo coeficiente de atrito (UBCA) e verificar se a mudança do pH do meio, ou a alteração da concentração de sílica na água, diminui o runningin, tempo necessário para o sistema entrar em regime estacionário, do coeficiente de atrito. Os ensaios foram realizados na configuração de ensaio tribológico esfera contra disco, no qual a esfera foi de nitreto de silício e o disco de alumina, sob carga normal de 54 N e velocidade de deslizamento de 1 m/s. A água utilizada nos ensaios foi destilada e deionizada, e a sílica coloidal amorfa, sem porosidade e de tamanho médio de partícula de 12 nanômetros foi a Aerosil® 200. A esfera de nitreto de silício, adquirida comercialmente, e o disco de alumina, foi proveniente de trabalhos anteriores. Todos os materiais foram caracterizados quanto a densidade. Algumas propriedades mecânicas como dureza, módulo de elasticidade e tenacidade à fratura foram determinadas. Nos ensaios lubrificados com água onde o pH foi controlado, o sistema atingiu o regime com valores de coeficiente de atrito da ordem de milésimos, exceto quando o pH da água era muito baixo ou muito alto. Em hidrossol o coeficiente de atrito chegou a unidades de milésimos, mas quando se aumenta a concentração de sílica coloidal, também, aumenta o desgaste nas superfícies. O disco de alumina sempre apresentou menor desgaste do que a esfera de nitreto de silício, em todas as condições estudadas.
Titre en anglais
Ultra low friction coefficient in sliding of Al2O3-Si3O3: effects of chemical variables (pH and concentration of colloidal silica).
Mots-clés en anglais
Alumina
Ceramics
Friction
Silicon nitride
Ultra low friction
Water
Wear
Resumé en anglais
The objective of this work was to investigate the tribological behavior of the ceramic pair alumina-silicon nitride, sliding on the water with controlled pH and in a suspension with different concentrations of colloidal silica in water, and verify the possibility of achieving a friction coefficient in the order of thousandths (μ < 0.01), here called ultra low friction coefficient (ULFC) and verify if the change of pH or changing the concentration of silica in the water, decreases the running-in, time required for the system reach the steady state of friction coefficient. The tests were conducted in a pin on disc setup in which the ball was made on silicon nitride and the disc of alumina, under normal load of 54 N and a sliding velocity of 1 m/s. The water used in the experiments was distilled and deionized. The amorphous silica, without porosity and average particle size of 12 nanometers was Aerosil ® 200. The ball of silicon nitride, was purchased commercially, and the alumina disk was recycled from previous works, all materials were characterized by density. Some mechanical properties such as hardness, elastic modulus and fracture toughness were determined. In tests with controlled pH water the system has reached the friction coefficient of the order of thousandths, except when the pH of the water was too low or too high. In hydrossol the friction coefficient reached units of thousandths, but when increasing the concentration of colloidal silica also increases the wear in the surfaces. The alumina disc always showed less wear than the ball of silicon nitride, in all conditions studied.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2012-11-27
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.