Disertación de Maestría
DOI
10.11606/D.3.2010.tde-23052011-111849
Documento
Autor
Nombre completo
Renato Lucato Gimenez
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Director
Tribunal
Sinatora, Amilton (Presidente)
Figueroa, Carlos Alejandro
Tanaka, Deniol Katsuki
Título en portugués
Sólidos viscoelásticos: área de hemiesferas de borracha contra uma superfície de vidro.
Palabras clave en portugués
Adesão
Área de contato
Hemiesferas de borracha
Tempo de exposição
Resumen en portugués
Neste trabalho estudou-se a variação da área de contato de hemiesferas de borracha contra uma superfície plana de vidro, variando-se a força de compressão aplicada, o tempo de aplicação da força e a força de separação das superfícies em contato. Os experimentos foram realizados com quatro borrachas de módulos de elasticidade 16,8, 5,77, 5,42 e 2,64 MPa e durezas de 87, 68, 57 e 44 Shore A, respectivamente. Para borrachas de dureza mais elevada, a variação da área de contato é menor para um mesmo carregamento de referência. Para borrachas com maior módulo viscoso, maior é a variação da área de contato em função do tempo de exposição e maior a força de separação entre as superfícies. Os resultados reafirmam o modelo de Jonhson, Kendall e Roberts para o contato com baixos carregamentos de esferas de borracha e contribui para o entendimento da área de contato em função do tempo de exposição ao carregamento, onde a variação chegou a 23% para a borracha de maior módulo viscoso.
Título en inglés
Viscoelastic solids: rubber hemisphere contact area with a flat glass plate.
Palabras clave en inglés
Adhesion
Contact area
Exposure time
Rubber hemisphere
Resumen en inglés
Contact area variation and separation forces of rubber hemispheres against a flat glass plate were studied with increasing normal forces and load exposure time. The experiments were performed on four different rubbers with Youngs modulus of 16.8, 5.77, 5.42 e 2.64 MPa and hardness of 87, 68, 57and 44 Shore A, respectively. For higher hardness rubbers, the contact area variation is smaller for the same load parameters. For higher viscous modulus rubber, the contact area variation over time is higher and it is also higher the surface separation force required. The results found are in agreement with Johnson, Kendall and Roberts model for the contact at low loads of rubber spheres and it does a contribution for the understanding of contact area due to load exposure time where variation reached up to 23% for the higher viscous modulus rubber.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-05-30
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.